Non-destructive sans investigation of in 738 turbine blades after high-temperature operation
- 1.
SYSNO ASEP 0105647 Druh ASEP G - Konferenční sborník (mezinárodní konf.) Zařazení RIV Není vybrán druh dokumentu Název Non-destructive sans investigation of in 738 turbine blades after high-temperature operation Překlad názvu Nedestruktivní SANS vyšetřování 738 turbinových lopatek po práci při vysoké teplotě Tvůrce(i) Marinčák, Vojtěch (UJF-V)
Strunz, Pavel (UJF-V) RID, ORCID, SAI
Šaroun, Jan (UJF-V) RID, ORCID, SAI
Ryukhtin, Vasyl (UJF-V) RID, ORCID, SAI
Lukáš, Petr (UJF-V) RID, ORCID, SAI
Cassi, L. (IT)
Ceschini, G. F. (IT)
Rogante, M. (IT)Vyd. údaje Geneva, 2003 Poč.str. 6 s. Forma vydání CD - CD Akce Proceedings of the International Conference of Mechanical Behaviour of Materials. Datum konání 25.05.2003-29.05.2003 Místo konání Geneve Země CH - Švýcarsko Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova superalloy ; SANS Vědní obor RIV BM - Fyzika pevných látek a magnetismus CEP KSK1010104 GA AV ČR - Akademie věd GA202/03/0891 GA ČR - Grantová agentura ČR Anotace The gas reactor turbine blades produced from the Inconel 738 nickel-base superalloy were studied with the aim to assess the influence of high-temperature operation fatigue on the microstructure. High-resolution small-angle neutron scattering (SANS) provides an unique possibility of non-destructive characterization of precipitates in the blades. Two turbine blades in as-cast state and after operation were compared at different positions along their edge, where different thermal and stress loads are expected. Size distributions and relative volume fractions of gamma´-precipitates were evaluated from measured SANS spectra for each blade and individual position. It was found that the precipitate volume fraction increases towards the tip of both blades. The blade after operation exhibits a significant increase of the average size and volume of precipitates with respect to the as-cast blade, which can be explained by expected stronger precipitate coarsening under higher stresses. The precipitate size varied along the blade in the as-cast state. The first results indicate that the SANS method would be a very useful tool for non-destructive testing of fatigue in turbine blades. Pracoviště Ústav jaderné fyziky Kontakt Markéta Sommerová, sommerova@ujf.cas.cz, Tel.: 266 173 228 Rok sběru 2005
Počet záznamů: 1