Biocompatible and antibacterial gelatin-based polypyrrole cryogels

0524035 - ÚMCH 2021 RIV GB eng J - Článek v odborném periodiku
Milakin, Konstantin A. - Capáková, Z. - Acharya, Udit - Vajďák, J. - Morávková, Zuzana - Hodan, Jiří - Humpolíček, P. - Bober, Patrycja
Biocompatible and antibacterial gelatin-based polypyrrole cryogels.
Polymer. Roč. 197, 27 May (2020), s. 1-7, č. článku 122491. ISSN 0032-3861. E-ISSN 1873-2291
Grant CEP: GA ČR(CZ) GA18-04669S
Institucionální podpora: RVO:61389013
Klíčová slova: polypyrrole * gelatin * cryogels
Obor OECD: Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics
Impakt faktor: 4.430, rok: 2020
Způsob publikování: Omezený přístup
https://www.sciencedirect.com/science/article/pii/S0032386120303232?via%3Dihub

Polypyrrole-gelatin cryogels were synthesized by oxidative cryopolymerization of pyrrole in the presence of gelatin. Vibrational spectroscopy confirmed formation of doped polypyrrole. Mechanical and pore structure stability of the resulting macroporous materials (pore size 10–50 μm) was shown to increase with increasing of gelatin content in initial polymerization medium, reaching plateau at 6 wt%. Thermal stability of polypyrrole-gelatin cryogels was found to be enhanced in comparison to its individual components. Electrical conductivity of all prepared cryogels (2–5 S cm−1) was similar to that of conventional polypyrrole. Cytotoxicity of polypyrrole-gelatin cryogels was found to decrease with increasing of gelatin concentration in the initial reaction mixture. The cryogel obtained using 8 wt% of gelatin showed the lowest cytotoxic effect reaching only mild cytotoxicity at 100% extract concentration. Polypyrrole-gelatin gels showed significant level of antibacterial activity without additional antibacterial agents.