0307736 - ÚFM 2008 RIV CZ eng C - Konferenční příspěvek (zahraniční konf.)
Král, Lubomír - Čermák, Jiří
Changes of structure in Mg-Ni alloys after absorption and desorption of hydrogen.
[Strukturní změny ve slitinách Mg-Ni po absorpci a desorpci vodíku.]
METAL 2008. Sborník přednášek.. Ostrava: Tanger, 2008, paper no. 12. ISBN 978-80-254-1987-8.
[METAL 2008. Mezinárodní konference metalurgie a materiálů /17./. Hradec nad Moravicí (CZ), 13.05.2008-15.05.2008]
Grant CEP: GA ČR GA106/07/0010
Výzkumný záměr: CEZ:AV0Z20410507
Klíčová slova: hydrogen storage * Mg-Ni alloys * casting and ball milling
Kód oboru RIV: BJ - Termodynamika

This paper deals with changes of structure in Mg-Ni alloys after absorption and desorption of hydrogen. Experimental materials were prepared by two techniques – by casting and by ball milling and subsequent compacting to pellets. These materials were hydrogen-charged at elevated temperature and pressure. Materials were studied using the SEM Jeol JSM 6460 equipped with EDS/WDS analyzers. Formation of rectangular particles of MgNi2, nucleation of MgH2 at grain boundaries, and changes of Mg2Ni were observed. The so-called activation of hydrogen storage alloy is most likely due to fine particles that appear after the first hydrogen charging.

V práci byly studovány strukturní změny ve slitinách Mg-Ni po absorpci a desorpci vodiku. Experimentální materály byly připraveny dvěma způsoby – odlitím a mletím a lisováním do tablet. Tyto materiály byly navodíkovány při zvýšené teplotě a tlaku. Byly studovány pomocí SEM Jeol JSM 6460 s EDS/WDS analyzátory. Byla sledována tvorba obdélníkových částic MgNi2, nukleace MgH2 na hranicích zrn a změny Mg2Ni. Tzv. aktivace vodík absorbujícího prostředí je spojena pravděpodobně s velmi jemnými částicemi, které se objeví ve struktuře materiálů po prvním nabíjení vodíkem.
Trvalý link: http://hdl.handle.net/11104/0160410