Growth and scintillation characteristics of CeF.sub.3./sub., PrF.sub.3./sub. and NdF.sub.3./sub. single crystals

  1. 1.
    0100188 - FZU-D 20040168 RIV NL eng J - Článek v odborném periodiku
    Shimamura, K. - Víllora, E. G. - Nakakita, S. - Nikl, Martin - Ichinose, N.
    Growth and scintillation characteristics of CeF3, PrF3 and NdF3 single crystals.
    [Růst a scintilační charakteristiky nanokrystalů CeF3, PrF3 and NdF3]
    Journal of Crystal Growth. Roč. 264, 208-215 (2004), s. 208-215. ISSN 0022-0248. E-ISSN 1873-5002
    Grant CEP: GA MŠk 1P04ME716
    Výzkumný záměr: CEZ:AV0Z1010914
    Klíčová slova: Czochralski method * rare-earth compounds * scintillator materials
    Kód oboru RIV: BM - Fyzika pevných látek a magnetismus
    Impakt faktor: 1.707, rok: 2004

    CeF3, PrF3 and NdF3 single crystals with 1 inch in diameter have been grown under CF4 atmosphere by the modified Czochralski technique. PrF3 exhibited a single sharp emission at about 400 nm, with a light intensity comparable to that of BGO and a decay time of 510 ns. Lu-doping was effective to increase the luminescence efficiency of CeF3.

    Nanokrystaly CeF3, PrF3 a NdF3 o průměru 1mm byly vypěstovány v atmosféře CF4 modifikovanou metodou Czochralského. PrF3 ukázal jednu úzkou emisní čáru kolem 400 nm s intenzitou porovnatelnou s BGO a dobou života 510 ns. Dopování Lu bylo efektivní pro zvýšení luminiscenční účinnosti CeF3.