    0100169 - FZU-D 20040149 RIV NL eng J - Článek v odborném periodiku
    Kulykovskyy, Valeriy - Boháč, Petr - Franc, František - Chvostová, Dagmar - Deyneka, Alexander - Vorlíček, Vladimír - Jastrabík, Lubomír
    Degradation and stress evolution in a-C, a-C:H a Ti-C:H films.
    [Degradace a vývoj pnutí ve vrstvách a-C, a-C:H a Ti-C:H.]
    Surface and Coatings Technology. 142-144, - (2001), s. 702-706. ISSN 0257-8972
    Grant CEP: GA MŠk LN00A015
    Výzkumný záměr: CEZ:AV0Z1010914
    Klíčová slova: sputtering * diamond-like carbon * stress evolution * coating degradation
    Kód oboru RIV: BM - Fyzika pevných látek a magnetismus
    Impakt faktor: 1.236, rok: 2001

    Some observations of the stress evolution and degradations of diamond-like a-C, a-C:H and Ti-C (10-20 at.% of Ti) films deposited by magnetron sputtering of the C or Ti target in the Ar or Ar+CH4 gas mixture are presented. The compressive stress increased during several days for Ti-C:H films but not for a-C films. The growth of stress was accompanied by a decrease of optical constants n and k

    Jsou prezentována některá pozorování vývoje vnitřních pnutí a degradace diamantu podobných vrstev a-C, a-C:H a Ti-C (10-20 at.% Ti) deponovaných magnetronovým naprašováním z C nebo Ti targetů v Ar nebo směsi Ar+CH4. Tlaková pnutí rostla v průběhu několika dní ve filmech Ti-C:H, nerostla ve vrstvách a-C. Růst pnutí byl provázen poklesem optických konstant n a k