Deformation behaviour and fracture of Ni-base single crystals at simultaneous action of high-cycle fatigue and creep

0083408 - ÚFM 2008 RIV SK eng J - Článek v odborném periodiku
Kunz, Ludvík - Lukáš, Petr
Deformation behaviour and fracture of Ni-base single crystals at simultaneous action of high-cycle fatigue and creep.
[Deformační chování a lom monokrystalů Ni superslitin za simultánního působení únavy a creepu.]
Materiálové inžinierstvo - Materials Engineering. Roč. 14, č. 2 (2007), s. 15-20. ISSN 1335-0803
Grant CEP: GA ČR GA106/05/2112
Výzkumný záměr: CEZ:AV0Z20410507
Klíčová slova: CMSX-4 * CM186LC * Fatigue life * Constant lifetime diagram
Kód oboru RIV: JG - Hutnictví, kovové materiály

The resistance against high-cycle fatigue combined with creep of Ni base superalloy single crystals CMSX-4 and CM186LC was experimentally determined. Both the negative and beneficial influence of vibrations on the lifetime was found. An attempt was made to explain the observed behavior on the basis of transition effects taking place after stress changes and influencing the creep rate and by the change of fracture type from ductile to fatigue initiated.

Experimentálně byla studována vysokocyklová únavová odolnost niklových monokrystalických superslitin CMSX-4 a CM186LC v podmínkách vysokoteplotního creepu. Byl zjištěn jak pozitivní, tak i negativní vliv vibrací na životnost. Byl učiněn pokus vysvětlit pozorované chování na základě existence přechodových jevů, které nastávají po změně zatížení a které ovlivňují rychlost creepu a také změnou charakteru lomu z tvárného na únavově iniciovaný lom.