Low cycle fatigue of cast gamma-TiAl based alloys at high temperature

  1. 1.
    0354105 - UFM-A 2011 RIV CH eng J - Článek v odborném periodiku
    Petrenec, Martin - Šmíd, Miroslav - Kruml, Tomáš - Obrtlík, Karel - Polák, Jaroslav
    Low cycle fatigue of cast gamma-TiAl based alloys at high temperature.
    Key Engineering Materials. Roč. 452-453, - (2011), s. 421-424 ISSN 1013-9826
    Grant CEP: GA ČR GA106/07/0762; GA ČR GA106/08/1631
    Výzkumný záměr: CEZ:AV0Z20410507
    Klíčová slova: low cycle fatigue * lamellar TiAl alloys * high temperature * PSMs * fracture surface
    Kód oboru RIV: JL - Únava materiálu a lomová mechanika

    The low-cycle fatigue properties of cast nearly lamellar TiAl alloys with diverse Nb content at room temperature and 750°C were compared. Monotonic tensile curves,cyclic stress-strain curves and combined fatigue life curves were obtained at both temperatures. After cyclic straining the surface relief and the fracture surfaces were observed using scanning electron microscopy. The increase in Nb content significantly improves tensile properties and CSSCs at both temperatures.The combined fatigue life curves especially at 750°C are shifted to higher fatigue lives. The effect o Nb content on the tensile and cyclic strength is discussed in relation to the thickness of the lamellae. Persistent slip markings formed along interlamellar interfaces were predominant locations for fatigue cracks. At both temperatures and materials showed similar crack initiation and propagation behavior. The cracks initiated at surface or in sub-surface region creating smooth flat areas corresponding to the persistent slip bands.