Low cycle fatigue of austempered ductile cast iron alloyed with nickel at room and at depressed temperature
0331756 - UFM-A 2010 RIV SK eng J - Článek v odborném periodiku
Petrenec, Martin - Beran, Přemysl - Šmíd, Miroslav - Roupcová, Pavla - Tesařová, H.
Low cycle fatigue of austempered ductile cast iron alloyed with nickel at room and at depressed temperature.
Materiálové inžinierstvo - Materials Engineering. Roč. 16, 3a (2009), s. 1-6 ISSN 1335-0803.
[Degradácia konštrukčných materiálov 2009. Tatranská Lomnica, 02.09.2009-04.09.2009]
Grant CEP: GA AV ČR 1QS200410502
Výzkumný záměr: CEZ:AV0Z20410507; CEZ:AV0Z10480505
Klíčová slova: Low cycle fatigue * ADI with nickel alloying * Neutron diffraction * Fatigue crack initiation * Depressed temperature
Kód oboru RIV: JL - Únava materiálu a lomová mechanika
Total strain controlled tests have been performed on cylindrical specimens of austempered ductile cast iron (ADI) with the aim to compare cyclic plasticity and the fatigue life at temperatures 23°C and –45°C. The measurement of retained austenite by neutron diffraction before and after fatigue tests is used to discuss the cyclic stress-strain response. Cyclic hardening/softening curves, cyclic stress-strain curves and fatigue life curves were obtained for both temperatures. Cyclic stress-strain curve obtained at -45°C is shifted to higher stress amplitudes relative to room temperature curve. The fatigue life curves at both temperatures can be well approximated by the Manson-Coffin and Basquin laws.The Manson-Coffin curves are identical at both temperatures while the Basquin curve is shifted to longer fatigue life. Fatigue cracks initiated preferably from persistent slip markings at the interface of graphite nodule and the ausferrite matrix.