- 1.0491914 - ÚFM 2019 RIV US eng J - Článek v odborném periodiku
Šulák, Ivo - Obrtlík, Karel - Čelko, L. - Chráska, Tomáš - Jech, D. - Gejdoš, P.
Low cycle fatigue performance of Ni-based superalloy coated with complex thermal barrier coating.
Materials Characterization. Roč. 139, MAY (2018), s. 347-354. ISSN 1044-5803. E-ISSN 1873-4189
Grant CEP: GA ČR(CZ) GA15-20991S
Institucionální podpora: RVO:68081723 ; RVO:61389021
Klíčová slova: Inconel 713LC * Thermal barrier coating * High-temperature low cycle fatigue * Cyclic stress-strain curve * Fatigue live curves * Degradation mechanisms
Obor OECD: Audio engineering, reliability analysis; Audio engineering, reliability analysis (UFP-V)
Impakt faktor: 3.220, rok: 2018
Trvalý link: http://hdl.handle.net/11104/0286823 - 2.0482087 - ÚFM 2018 RIV GB eng J - Článek v odborném periodiku
Šulák, Ivo - Obrtlík, Karel
Effect of tensile dwell on high-temperature low-cycle fatigue and fracture behaviour of cast superalloy MAR-M247.
Engineering Fracture Mechanics. Roč. 185, NOV (2017), s. 92-100. ISSN 0013-7944. E-ISSN 1873-7315.
[ICMFM 2016 - International Colloquium on Mechanical Fatigue of Metals /18./. Gijón, 05.09.2016-07.09.2016]
Grant CEP: GA ČR(CZ) GA15-20991S
Institucionální podpora: RVO:68081723
Klíčová slova: Nickel-based superalloy * High-temperature low-cycle fatigue * Tensile dwell * Fatigue life * Damage mechanisms
Obor OECD: Audio engineering, reliability analysis
Impakt faktor: 2.580, rok: 2017
Trvalý link: http://hdl.handle.net/11104/0278857 - 3.0478233 - ÚFM 2018 RIV CH eng J - Článek v odborném periodiku
Obrtlík, Karel - Čelko, L. - Chráska, Tomáš - Šulák, Ivo - Gejdoš, P.
Effect of alumina-silica-zirconia eutectic ceramic thermal barrier coating on the low cycle fatigue behaviour of cast polycrystalline nickel-based superalloy at 900 °C.
Surface and Coatings Technology. Roč. 318, MAY (2017), s. 374-381. ISSN 0257-8972.
[RIPT - International Meeting on Thermal Spraying /7./. Limoges, 09.12.2015-12.12.2015]
Grant CEP: GA ČR(CZ) GA15-20991S
Institucionální podpora: RVO:68081723 ; RVO:61389021
Klíčová slova: Thermal barrier coating * Nickel-based superalloy * Plasma spraying * High temperature fatigue * Fatigue life * Cyclic stress-strain curve
Obor OECD: Audio engineering, reliability analysis; Audio engineering, reliability analysis (UFM-A); Audio engineering, reliability analysis (UFP-V)
Impakt faktor: 2.906, rok: 2017
Trvalý link: http://hdl.handle.net/11104/0274628 - 4.0467010 - ÚFM 2017 RIV SK eng J - Článek v odborném periodiku
Šulák, Ivo - Obrtlík, Karel - Čelko, L.
High-temperature low-cycle fatigue behaviour of HIP treated and untreated superalloy MAR-M247.
Kovové materiály. Roč. 54, č. 6 (2016), s. 471-481. ISSN 0023-432X. E-ISSN 1338-4252
Grant CEP: GA TA ČR(CZ) TA04011525; GA ČR(CZ) GA15-20991S
Institucionální podpora: RVO:68081723
Klíčová slova: hot isostatic pressing * high-temperature low cycle fatigue * fatigue life curves * Ni-based superalloy * dislocation structures * planar bands
Kód oboru RIV: JL - Únava materiálu a lomová mechanika
Impakt faktor: 0.366, rok: 2016
Trvalý link: http://hdl.handle.net/11104/0265258