- 1.0499226 - ÚFM 2019 RIV GB eng J - Článek v odborném periodiku
Šulák, Ivo - Obrtlík, Karel - Čelko, L. - Gejdoš, P. - Jech, D.
High-Temperature Low-Cycle Fatigue Behaviour of MAR-M247
Coated with Newly Developed Thermal and Environmental
Barrier Coating.
Advances in Materials Science and Engineering. Vol.2018, DEC (2018), č. článku 9014975. ISSN 1687-8434. E-ISSN 1687-8442
Grant CEP: GA MŠMT LM2015069
Institucionální podpora: RVO:68081723
Klíčová slova: FINITE-ELEMENT SIMULATION * NICKEL-BASED SUPERALLOY * MAR-M 247 * THERMOMECHANICAL FATIGUE * DEGRADATION
Obor OECD: Audio engineering, reliability analysis
Impakt faktor: 1.399, rok: 2018
Trvalý link: http://hdl.handle.net/11104/0292807 - 2.0491914 - ÚFM 2019 RIV US eng J - Článek v odborném periodiku
Šulák, Ivo - Obrtlík, Karel - Čelko, L. - Chráska, Tomáš - Jech, D. - Gejdoš, P.
Low cycle fatigue performance of Ni-based superalloy coated with complex thermal barrier coating.
Materials Characterization. Roč. 139, MAY (2018), s. 347-354. ISSN 1044-5803. E-ISSN 1873-4189
Grant CEP: GA ČR(CZ) GA15-20991S
Institucionální podpora: RVO:68081723 ; RVO:61389021
Klíčová slova: Inconel 713LC * Thermal barrier coating * High-temperature low cycle fatigue * Cyclic stress-strain curve * Fatigue live curves * Degradation mechanisms
Obor OECD: Audio engineering, reliability analysis; Audio engineering, reliability analysis (UFP-V)
Impakt faktor: 3.220, rok: 2018
Trvalý link: http://hdl.handle.net/11104/0286823 - 3.0478233 - ÚFM 2018 RIV CH eng J - Článek v odborném periodiku
Obrtlík, Karel - Čelko, L. - Chráska, Tomáš - Šulák, Ivo - Gejdoš, P.
Effect of alumina-silica-zirconia eutectic ceramic thermal barrier coating on the low cycle fatigue behaviour of cast polycrystalline nickel-based superalloy at 900 °C.
Surface and Coatings Technology. Roč. 318, MAY (2017), s. 374-381. ISSN 0257-8972.
[RIPT - International Meeting on Thermal Spraying /7./. Limoges, 09.12.2015-12.12.2015]
Grant CEP: GA ČR(CZ) GA15-20991S
Institucionální podpora: RVO:68081723 ; RVO:61389021
Klíčová slova: Thermal barrier coating * Nickel-based superalloy * Plasma spraying * High temperature fatigue * Fatigue life * Cyclic stress-strain curve
Obor OECD: Audio engineering, reliability analysis; Audio engineering, reliability analysis (UFM-A); Audio engineering, reliability analysis (UFP-V)
Impakt faktor: 2.906, rok: 2017
Trvalý link: http://hdl.handle.net/11104/0274628