Influence of pyrolysis temperature on fracture response in SiOC based composites reinforced by basalt woven fabric

SYSNO ASEP	0433976
Druh ASEP	J - Článek v odborném periodiku
Zařazení RIV	J - Článek v odborném periodiku
Poddruh J	Článek ve WOS
Název	Influence of pyrolysis temperature on fracture response in SiOC based composites reinforced by basalt woven fabric
Tvůrce(i)	Chlup, Zdeněk (UFM-A)_{RID, ORCID} Černý, Martin (USMH-B)_{RID, ORCID, SAI} Strachota, Adam (UMCH-V)_{RID, ORCID} Sucharda, Zbyněk (USMH-B) Halasová, Martina (UFM-A) Dlouhý, Ivo (UFM-A)_{RID, ORCID}
Celkový počet autorů	6
Zdroj.dok.	Journal of the European Ceramic Society. - : Elsevier - ISSN 0955-2219 Roč. 34, č. 14 (2014), s. 3389-3398
Poč.str.	10 s.
Jazyk dok.	eng - angličtina
Země vyd.	GB - Velká Británie
Klíč. slova	Fracture behaviour ; CMCs ; Pyrolysis ; Basalt fibre ; Polysiloxane
Vědní obor RIV	JL - Únava materiálu a lomová mechanika
Vědní obor RIV – spolupráce	Ústav struktury a mechaniky hornin - Kompozitní materiály Ústav makromolekulární chemie - Keramika, žáruvzdorné materiály a skla
CEP	GAP107/12/2445 GA ČR - Grantová agentura ČR
	ED1.1.00/02.0068 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy
Institucionální podpora	UFM-A - RVO:68081723 ; USMH-B - RVO:67985891 ; UMCH-V - RVO:61389013
UT WOS	000340222800018
DOI	10.1016/j.jeurceramsoc.2014.03.003
Anotace	The fracture resistance of ceramic based composites reinforced by various ceramic fibres can be dramatically enhanced when an efficient fracture mechanism takes place during the crack propagation. Presented work shows an effect of the pyrolysis temperature of the composite matrix on the fracture behaviour of the composite. The matrix is formed from the polysiloxane resin precursor and the reinforcement is a basalt woven fabric. The temperature range under investigation was from 600°C, where the onset of fracture properties were observed up to 800°C. Above this temperature basalt fibres suffer by rapid degradation of the microstructure. The optimum stage of the polysiloxane resin transformation maximizing the fracture resistance of the composite was identified. The fractographic analysis of the fracture surfaces revealed the differences in the acting fracture mechanism.