Počet záznamů: 1
The effect of treatment of powder precursor on the properties of compacted Mg-4Y-3Re alloy
- 1.
SYSNO ASEP 0578841 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název The effect of treatment of powder precursor on the properties of compacted Mg-4Y-3Re alloy Tvůrce(i) Dvorský, Drahomír (FZU-D) ORCID
Kubásek, J. (CZ)
Nečas, D. (CZ)
Čavojský, M. (SK)
Drahokoupil, Jan (FZU-D) RID, ORCID
Vojtěch, D. (CZ)Celkový počet autorů 6 Číslo článku 045001 Zdroj.dok. Journal of Engineering Materials and Technology-Transactions of the Asme - ISSN 0094-4289
Roč. 145, č. 4 (2023)Poč.str. 8 s. Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova materials processing ; mechanical behavior ; metals ; powder metallurgy ; magnesium ; extrusion ; composites ; microstructure property relationships Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering Způsob publikování Omezený přístup Institucionální podpora FZU-D - RVO:68378271 UT WOS 001088402700007 DOI 10.1115/1.4063059 Anotace Powder metallurgy products display superior performance compared to traditionally cast ingots. The results show that distinct microstructures were produced, and their impact on mechanical and corrosion properties was evaluated. The results indicate that milling and chemical treatment increase the yield strength of the material by up to 34 MPa but decrease the elongation by up to 5%. On the other hand, heat treatment increases the elongation by up to 7% but decreases the yield strength by up to 36 MPa. Corrosion resistance is improved especially by chemical and heat treatment of powders, where the corrosion rate was observed to decrease by up to 50% in comparison to the value of product from atomized powder. This provides an opportunity to tailor the mechanical and corrosion properties of these materials to meet specific applications. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2024 Elektronická adresa https://doi.org/10.1115/1.4063059
Počet záznamů: 1