Highly regular LIPSS on thin molybdenum films: optimization and generic criteria
- 1.
SYSNO ASEP 0571931 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Highly regular LIPSS on thin molybdenum films: optimization and generic criteria Tvůrce(i) Sládek, Juraj (FZU-D) ORCID
Hlinomaz, Kryštof (FZU-D)
Mirza, M. Inam (FZU-D) ORCID
Levy, Yoann (FZU-D)
Derrien, Thibault (FZU-D) ORCID
Cimrman, Martin (FZU-D) ORCID
Nagisetty, S.S. (DE)
Čermák, Jan (FZU-D) RID, SAI, ORCID
Stuchlíková, The-Ha (FZU-D) RID, ORCID
Stuchlík, Jiří (FZU-D) RID, ORCID
Bulgakova, Nadezhda M. (FZU-D) ORCIDCelkový počet autorů 11 Číslo článku 2883 Zdroj.dok. Materials. - : MDPI
Roč. 16, č. 7 (2023)Poč.str. 12 s. Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova laser-induced periodic surface structures ; highly regular LIPSS ; thin film ; molybdenum Vědní obor RIV BH - Optika, masery a lasery Obor OECD Optics (including laser optics and quantum optics) CEP EF15_003/0000445 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy EF15_006/0000674 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Open access Institucionální podpora FZU-D - RVO:68378271 UT WOS 000970178700001 EID SCOPUS 85152764279 DOI 10.3390/ma16072883 Anotace A systematic experimental study was performed to determine laser irradiation conditions for the large-area fabrication of highly regular laser-induced periodic surface structures (HR-LIPSS) on a 220 nm thick Mo film deposited on fused silica. The LIPSS were fabricated by scanning a linearly polarized, spatially Gaussian laser beam at 1030 nm wavelength and 1.4 ps pulse duration over the sample surface at 1 kHz repetition rate. Scanning electron microscope images of the produced structures were analyzed using the criterion of the dispersion of the LIPSS orientation angle (DLOA). Favorable conditions, in terms of laser fluence and beam scanning overlaps, were identified for achieving DLOA values <10∘ . To gain insight into the material behavior under these irradiation conditions, a theoretical analysis of the film heating was performed, and surface plasmon polariton excitation is discussed. A possible effect of the film dewetting from the dielectric substrate is deliberated. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2024 Elektronická adresa https://hdl.handle.net/11104/0342825