Preparation of Ti3SiC2 MAX phase from Ti, TiC, and SiC by SPS
- 1.
SYSNO ASEP 0565846 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Preparation of Ti3SiC2 MAX phase from Ti, TiC, and SiC by SPS Tvůrce(i) Csáki, Štefan (UFP-V) ORCID
Lukáč, František (UFP-V) ORCID
Veverka, Jakub (UFP-V) ORCID
Chráska, Tomáš (UFP-V) RID, ORCIDCelkový počet autorů 4 Zdroj.dok. Ceramics International. - : Elsevier - ISSN 0272-8842
Roč. 48, č. 19 (2022), s. 28391-28395Poč.str. 5 s. Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova Dilatometry ; MAX phase ; Porosity ; Sintering ; sps Vědní obor RIV JK - Koroze a povrchové úpravy materiálů Obor OECD Materials engineering CEP GA19-11275S GA ČR - Grantová agentura ČR Způsob publikování Omezený přístup Institucionální podpora UFP-V - RVO:61389021 UT WOS 000877931900002 EID SCOPUS 85132539786 DOI 10.1016/j.ceramint.2022.06.149 Anotace Ti3SiC2 MAX phase was prepared from Ti, TiC, and SiC using spark plasma sintering. Three sintering temperatures, namely 1450, 1550, and 1600 °C were employed. The effect of the atmosphere, dwell time, and SiC grain size were studied. The prepared samples were subjected to XRD, Vickers hardness, and SEM analyses. Phase composition of the samples revealed that a maximum MAX phase content of ∼90 wt% is achieved at the sintering temperature of 1550 °C. TiC (∼9 wt%) and small amount of SiC were identified as secondary phases. Values of the Vickers hardness exhibited a steady decrease with an increasing sintering temperature from 704 HV at 1450 °C to 544 HV at 1600 °C due to the reduction of the TiC content in the sample. The porosity of the samples with the highest Ti3SiC2 content reached 5%. The coefficient of thermal expansion fell into the interval from 9.8 to 11 × 10−6 K−1. Pracoviště Ústav fyziky plazmatu Kontakt Vladimíra Kebza, kebza@ipp.cas.cz, Tel.: 266 052 975 Rok sběru 2023 Elektronická adresa https://www.sciencedirect.com/science/article/pii/S0272884222021526?via%3Dihub
Počet záznamů: 1