Fatigue crack growth characterization of Inconel 718 after additive manufacturing by laser powder bed fusion and heat treatment
- 1.
SYSNO ASEP 0562906 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Fatigue crack growth characterization of Inconel 718 after additive manufacturing by laser powder bed fusion and heat treatment Tvůrce(i) Gruber, K. (PL)
Szymczyk-Ziolkowska, P. (PL)
Dziuba, S. (PL)
Duda, S. (PL)
Zielonka, P. (PL)
Seitl, Stanislav (UFM-A) RID, ORCID
Lesiuk, G. (PL)Celkový počet autorů 7 Číslo článku 107287 Zdroj.dok. International Journal of Fatigue. - : Elsevier - ISSN 0142-1123
Roč. 166, JAN (2023)Poč.str. 13 s. Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova Inconel 718 ; Laser powder bed fusion ; Hot isostatic pressing ; Fatigue crack growth rate ; Mean stress effect Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering Způsob publikování Open access Institucionální podpora UFM-A - RVO:68081723 UT WOS 000863519600002 EID SCOPUS 85138475668 DOI 10.1016/j.ijfatigue.2022.107287 Anotace Numerous studies were conducted on the tension-compression fatigue behavior of Inconel 718 (IN718) fabri-cated with laser powder bed fusion (LPBF). Contrary, only a few fatigue crack growth rate (FCGR) studies are available in the literature. Considering the above, LPBF manufactured IN718 is heat treated in variants including (H) and excluding (A) hot isostatic pressing. FCGR tests are performed at stress ratios R = 0.1 and R = 0.5. Both variants show similar FCGR and fracture modes at both stress ratios, despite a significant difference in ductility. Furthermore, A and H show similar FCGR at R = 0.1 and better performance at R = 0.5 compared to wrought IN718. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2024 Elektronická adresa https://www.sciencedirect.com/science/article/pii/S0142112322005370?via%3Dihub