Experimental Phase Diagram of the Ag-Se-Sn System at 250, 400 and 550 degrees C
- 1.
SYSNO ASEP 0556171 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Experimental Phase Diagram of the Ag-Se-Sn System at 250, 400 and 550 degrees C Tvůrce(i) Zobač, Ondřej (UFM-A) ORCID
Richter, K. (AT)
Kroupa, Aleš (UFM-A) RID, ORCIDCelkový počet autorů 3 Zdroj.dok. Journal of Phase Equilibria and Diffusion. - : Springer - ISSN 1547-7037
Roč. 43, č. 1 (2022), s. 32-42Poč.str. 11 s. Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova saturated solid-solutions ; crystal-structure ; thermoelectric performance ; thermodynamic properties ; silver ; Ag-Se-Sn phase diagram ; Ag8SeSn6 phase ; sem-edx ; xrd Vědní obor RIV BJ - Termodynamika Obor OECD Thermodynamics CEP GC18-25660J GA ČR - Grantová agentura ČR Způsob publikování Omezený přístup Institucionální podpora UFM-A - RVO:68081723 UT WOS 000748446400001 EID SCOPUS 85123883871 DOI 10.1007/s11669-022-00937-w Anotace The ternary phase diagram Ag-Se-Sn was re-investigated experimentally. The current study was designed to contribute to a better understanding of phase equilibria in isothermal sections at 250, 400 and 550 degrees C using long-term annealed samples. An intermediate liquid region was observed at 550 degrees C in agreement with older published vertical sections of the ternary phase diagram Ag-Se-Sn. A huge homogeneity range in ternary intermetallic phase Ag8Se6Sn at 250 degrees C was determined by SEM/EDX analysis of long term annealed samples and confirmed by XRD measurements. A second ternary phase AgSe2Sn was observed at each of the studied temperatures. Complete isothermal sections at 250, 400 and 550 degrees C were constructed in the scope of this paper. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2023 Elektronická adresa https://link.springer.com/article/10.1007/s11669-022-00937-w
Počet záznamů: 1