Effect of laser shock peening parameters on residual stresses and corrosion fatigue of AA5083
- 1.
SYSNO ASEP 0554586 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Effect of laser shock peening parameters on residual stresses and corrosion fatigue of AA5083 Tvůrce(i) Kaufman, Jan (FZU-D) ORCID
Špirit, Z. (CZ)
Vasudevan, V.K. (US)
Steiner, M.A. (US)
Mannava, S.R. (US)
Brajer, Jan (FZU-D) ORCID
Pína, L. (CZ)
Mocek, Tomáš (FZU-D) RID, ORCID, SAICelkový počet autorů 8 Číslo článku 1635 Zdroj.dok. Metals. - : MDPI
Roč. 11, č. 10 (2021)Poč.str. 10 s. Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova LSP ; LPwC ; residual stress ; corrosion fatigue ; aluminium alloy ; sensitization ; intergranular corrosion Vědní obor RIV BH - Optika, masery a lasery Obor OECD Optics (including laser optics and quantum optics) CEP EF15_006/0000674 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Open access Institucionální podpora FZU-D - RVO:68378271 UT WOS 000714005200001 EID SCOPUS 85116989949 DOI 10.3390/met11101635 Anotace Aluminium alloy 5083 was subjected to Laser Shock Peening both with (LSP) and without protective coating (LPwC) at multiple pulse densities. A second LPwC treatment was conducted fully submersed under water, in addition to the standard laminar water flow condition. The results show that compressive residual stresses were generated in all cases, although their character varied depending on the peening strategy and method of confinement. In all cases, higher pulse density lead to an increase in compressive stresses with a saturation point of −325 MPa at 1089 p/cm2 for the LPwC treatments. Corrosion fatigue testing of sensitized samples then showed 59% and 69% improvement in fatigue strength after the LSP and LPwC treatments, respectively. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2022 Elektronická adresa http://hdl.handle.net/11104/0329286
Počet záznamů: 1