High susceptibility of 3D-printed Ti-6Al-4V alloy to hydrogen trapping and embrittlement
- 1.
SYSNO ASEP 0546224 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název High susceptibility of 3D-printed Ti-6Al-4V alloy to hydrogen trapping and embrittlement Tvůrce(i) Kačenka, Z. (CZ)
Roudnická, Michaela (FZU-D) ORCID
Ekrt, Ondřej (FZU-D) ORCID
Vojtěch, D. (CZ)Celkový počet autorů 4 Číslo článku 130334 Zdroj.dok. Materials Letters. - : ELSEVIER SCIENCE BV - ISSN 0167-577X
Roč. 301, Oct. (2021)Poč.str. 4 s. Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova hydrogen ; hydrogen trapping ; titanium ; Ti-6Al-4V ; 3D printing Vědní obor RIV BM - Fyzika pevných látek a magnetismus Obor OECD Condensed matter physics (including formerly solid state physics, supercond.) Způsob publikování Omezený přístup Institucionální podpora FZU-D - RVO:68378271 UT WOS 000675889100007 DOI 10.1016/j.matlet.2021.130334 Anotace Today, 3D-printed titanium components become increasingly utilized in various fields thanks to the great shape freedom that 3D printing offers, especially in aerospace, automotive, power industry, or in the fabrication of progressive medical implants. However, in this paper, we demonstrate a high susceptibility of 3D-printed Ti-6Al-4V alloy to hydrogen trapping and embrittlement supported by its specific microstructure. 3D-printed (Selective Laser Melted) and wrought Ti-6Al-4V alloys were electrochemically hydrogenated under the same parameters. In comparison to conventionally prepared wrought alloy, the content of hydrogen trapped in the 3D-printed alloy after electrochemical charging was twofold (5458 ppm vs 2857 ppm, respectively). Heat treatment slightly decreased the susceptibility to hydrogen trapping. Even though, a complete embrittlement was observed for all 3D-printed samples. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2022 Elektronická adresa https://doi.org/10.1016/j.matlet.2021.130334
Počet záznamů: 1