Mechanical and structural properties of bulk magnesium materials prepared via spark plasma sintering
- 1.
SYSNO ASEP 0546040 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Mechanical and structural properties of bulk magnesium materials prepared via spark plasma sintering Tvůrce(i) Březina, M. (CZ)
Hasoňová, M. (CZ)
Fintová, Stanislava (UFM-A) ORCID
Doležal, P. (CZ)
Rednyk, Andrii (UFP-V)
Wasserbauer, J. (CZ)Celkový počet autorů 6 Číslo článku 102569 Zdroj.dok. Materials Today Communications. - : Elsevier - ISSN 2352-4928
Roč. 28, SEP (2021)Poč.str. 8 s. Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova in-situ precipitation ; pure magnesium ; plastic-deformation ; grain-refinement ; alloy ; temperature ; mg ; extrusion ; evolution ; Magnesium powder metallurgy ; sps ; Three-point bending ; Hardness ; Microhardness ; Microstructure Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering Vědní obor RIV – spolupráce Ústav fyziky plazmatu - Hutnictví, kovové materiály CEP EF16_013/0001823 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Omezený přístup Institucionální podpora UFM-A - RVO:68081723 ; UFP-V - RVO:61389021 UT WOS 000697048000004 EID SCOPUS 85108841964 DOI 10.1016/j.mtcomm.2021.102569 Anotace Field-assisted sintering is a modern approach to novel magnesium materials preparation, however, it is unclear whether it is better to sinter green compact or loose powder. This work focuses on preparing bulk materials from loose and cold-compacted magnesium powder through a field-assisted sintering technique spark plasma sintering (SPS). Green compacts were prepared under a series of compacting pressures from 100 MPa to 500 MPa. SPS was performed at 400 degrees C, 500 degrees C, and 600 degrees C applying additional pressure of 100 MPa during the sintering process. Prepared materials were analysed regarding their microstructure, hardness, and micmhardness and through the three-point bending test and fractography. The green compacts porosity decreased with increased cold-compaction pressure. The SPS positively affected porosity and mechanical properties only in loose powder and the lowest cold-compacted green compacts. Increasing cold compaction pressure of the green compacts above 200 MPa is therefore unfavourable for further SPS processing. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2022 Elektronická adresa https://www.sciencedirect.com/science/article/pii/S2352492821005602?via%3Dihub
Počet záznamů: 1