Thermal analysis of Al droplet crystallization and modeling of the nucleation process: how to interpret experimental data?

  1. 1.
    SYSNO ASEP0545284
    Druh ASEPA - Abstrakt
    Zařazení RIVO - Ostatní
    NázevThermal analysis of Al droplet crystallization and modeling of the nucleation process: how to interpret experimental data?
    Tvůrce(i) Kožíšek, Zdeněk (FZU-D) RID, ORCID, SAI
    Král, Robert (FZU-D) RID, ORCID
    Zemenová, Petra (FZU-D) RID, ORCID
    Celkový počet autorů3
    Zdroj.dok.American Conference on Crystal Growth and Epitaxy (ACCGE-22). - Virtual : ACCGE, 2021
    S. 295-295
    Poč.str.1 s.
    Forma vydáníOnline - E
    AkceAmerican Conference on Crystal Growth and Epitaxy (ACCGE-22) / 20th US Workshop on Organometallic Vapor Phase Epitaxy OMVPE /20./
    Datum konání02.08.2021 - 04.08.2021
    Místo konáníVirtual Conference
    ZeměUS - Spojené státy americké
    Typ akceWRD
    Jazyk dok.eng - angličtina
    Země vyd.US - Spojené státy americké
    Klíč. slovaDSC ; crystallization ; nucleation ; aluminum
    Vědní obor RIVBM - Fyzika pevných látek a magnetismus
    Obor OECDCondensed matter physics (including formerly solid state physics, supercond.)
    CEPEF16_019/0000760 GA MŠk - Ministerstvo školství, mládeže a tělovýchovy
    Institucionální podporaFZU-D - RVO:68378271
    AnotaceThe crystallization of Aluminum (Al) droplet was detected by the Differential Scanning Calorimetry (DSC) at the temperature Tc = 642 C (undercooling 18 K) using broad range of cooling rates 2-20 K/min. In the next step, the repeated DSC measurements at the isothermal conditions with undercooling of ca. 6 K discovered that the crystallization event occured after relatively long time delay 10-50 min. Experimental data confirmed the stochastic nature of crystal nucleation similarly to other systems. We analyzed the DSC data using the Johnson-Mehl-Avrami (JMA) model and also via numerical solution of the standard kinetic model of nucleation. In this case, the JMA model fails as the dimensionality of the growth is unrealistic. The crystallization probably occurs by a two-step mechanism, i.e. when the structure of small sub-critical clusters differs from the larger ones and thus the nucleation kinetics is slow.