Advantageous Description of Short Fatigue Crack Growth Rates in Austenitic Stainless Steels with Distinct Properties
- 1.
SYSNO ASEP 0544868 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Advantageous Description of Short Fatigue Crack Growth Rates in Austenitic Stainless Steels with Distinct Properties Tvůrce(i) Trávníček, Lukáš (UFM-A) RID, ORCID
Kuběna, Ivo (UFM-A) RID, ORCID
Mazánová, Veronika (UFM-A)
Vojtek, Tomáš (UFM-A) ORCID
Polák, Jaroslav (UFM-A) RID, ORCID
Hutař, Pavel (UFM-A) RID, ORCID
Šmíd, Miroslav (UFM-A) RID, ORCIDCelkový počet autorů 7 Číslo článku 475 Zdroj.dok. Metals. - : MDPI
Roč. 11, č. 3 (2021)Poč.str. 20 s. Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova short fatigue crack ; large scale yielding ; low cycle fatigue ; J-integral ; austenitic stainless steel ; residual lifetime prediction Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering CEP GJ19-25591Y GA ČR - Grantová agentura ČR Způsob publikování Open access Institucionální podpora UFM-A - RVO:68081723 UT WOS 000633884600001 EID SCOPUS 85102368809 DOI 10.3390/met11030475 Anotace In this work two approaches to the description of short fatigue crack growth rate under large-scale yielding condition were comprehensively tested: (i) plastic component of the J-integral and (ii) Polak model of crack propagation. The ability to predict residual fatigue life of bodies with short initial cracks was studied for stainless steels Sanicro 25 and 304L. Despite their coarse microstructure and very different cyclic stress-strain response, the employed continuum mechanics models were found to give satisfactory results. Finite element modeling was used to determine the J-integrals and to simulate the evolution of crack front shapes, which corresponded to the real cracks observed on the fracture surfaces of the specimens. Residual fatigue lives estimated by these models were in good agreement with the number of cycles to failure of individual test specimens strained at various total strain amplitudes. Moreover, the crack growth rates of both investigated materials fell onto the same curve that was previously obtained for other steels with different properties. Such a aster curve was achieved using the plastic part of J-integral and it has the potential of being an advantageous tool to model the fatigue crack propagation under large-scale yielding regime without a need of any additional experimental data. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2022 Elektronická adresa https://www.mdpi.com/2075-4701/11/3/475