Počet záznamů: 1
Oxygen effect in NO direct decomposition over K/Co-Mg-Mn-Al mixed oxide catalyst–Temperature programmed desorption study.
- 1.
SYSNO ASEP 0543504 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Oxygen effect in NO direct decomposition over K/Co-Mg-Mn-Al mixed oxide catalyst–Temperature programmed desorption study. Tvůrce(i) Pacultová, K. (CZ)
Klegová, A. (CZ)
Karásková, K. (CZ)
Fridrichová, D. (CZ)
Bílková, T. (CZ)
Koštejn, Martin (UCHP-M) RID, SAI, ORCID
Obalová, L. (CZ)Číslo článku 111695 Zdroj.dok. Molecular Catalysis. - : Elsevier - ISSN 2468-8231
Roč. 510, JUN 2021 (2021)Poč.str. 16 s. Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova mechanism ; mixed oxide ; oxygen effect ; NO Vědní obor RIV CI - Průmyslová chemie a chemické inženýrství Obor OECD Chemical process engineering CEP GA18-19519S GA ČR - Grantová agentura ČR Způsob publikování Open access s časovým embargem (01.07.2023) Institucionální podpora UCHP-M - RVO:67985858 UT WOS 000713699300002 EID SCOPUS 85108300444 DOI 10.1016/j.mcat.2021.111695 Anotace Co-Mg-Mn-Al mixed oxide with or without K was prepared and characterized by XPS, TPR H2, TPD NO, TPD O2 and TPD NO+O2. NO decomposition was performed over catalyst activated in different atmosphere (N2, He, O2). Presence of oxygen during activation changed the course of surface stabilization but did not affect NO conversion achieved at steady state. O2 desorbed as a reaction product does not affect the reaction rate for NO inlet concentration of 400 - 8000 ppm, but presence of O2 in inlet gas mixture (0.05 - 3 mol.%) has significant inhibiting effect. Transition metals in octahedral coordination represent sites for NO chemisorption, while potassium ensures NO oxidation to surface nitrites, which are indispensable reactive species. Oxygen desorption was the slowest reaction step, while N2 desorption was fast. Oxygen inhibition was ascribed to oxidation of NO* species on the octahedral Co3+ and Mn3+ to more stable surface nitrates making NO* species as limiting reactant. Pracoviště Ústav chemických procesů Kontakt Eva Jirsová, jirsova@icpf.cas.cz, Tel.: 220 390 227 Rok sběru 2022 Elektronická adresa http://hdl.handle.net/11104/0320699
Počet záznamů: 1