On the dynamics of twinning in magnesium micropillars

  1. 1.
    SYSNO ASEP0542590
    Druh ASEPJ - Článek v odborném periodiku
    Zařazení RIVJ - Článek v odborném periodiku
    Poddruh JČlánek ve WOS
    NázevOn the dynamics of twinning in magnesium micropillars
    Tvůrce(i) Máthis, K. (CZ)
    Knapek, Michal (UJF-V) ORCID
    Šiška, Filip (UFM-A) RID, ORCID
    Harcuba, P. (CZ)
    Ugi, D. (HU)
    Ispanovity, P. D. (HU)
    Groma, I. (HU)
    Shin, K. S. (KR)
    Celkový počet autorů8
    Číslo článku109563
    Zdroj.dok.Materials and Design - ISSN 0264-1275
    Roč. 203, MAY (2021)
    Poč.str.10 s.
    Forma vydáníTištěná - P
    Jazyk dok.eng - angličtina
    Země vyd.GB - Velká Británie
    Klíč. slovamagnesium ; compression ; twinning ; finite element modeling ; scanning electron microscopy
    Vědní obor RIVBM - Fyzika pevných látek a magnetismus
    Obor OECDMaterials engineering
    Vědní obor RIV – spolupráceÚstav fyziky materiálu - Hutnictví, kovové materiály
    CEPGA18-07140S GA ČR - Grantová agentura ČR
    EF16_013/0001794 GA MŠk - Ministerstvo školství, mládeže a tělovýchovy
    Způsob publikováníOpen access
    Institucionální podporaUFM-A - RVO:68081723 ; UJF-V - RVO:61389005
    UT WOS000640368300007
    EID SCOPUS85101168309
    DOI10.1016/j.matdes.2021.109563
    AnotaceMicro-deformation testing has recently gained far-reaching scientific importance as it provides intrinsic information on the dynamics of plastic deformation which is concealed when bulk materials are tested. In this work, single-crystal Mg micropillars favorably oriented for mechanical twinning were tested in compression with con-current scanning electron microscopy imaging. The experimental data were complemented by the finite element modeling in order to reveal the underlying physical background of the observed twinning dynamics. It was shown that the thickness of a twin should reach a critical value before triggering the nucleation of another twin to accommodate further strain. Nucleation and growth are repeated until the twins form throughout the whole micropillar, from top to bottom. Afterwards, the thickening and coalescence of all these twins take place until the entire micropillar volume is twinned. In addition, a line-by-line analysis of the scanning electron microscopy images was employed to reveal the twin lateral growth rates, which were shown to be on the order of 10(-5)-10(-4) m/s.