Polydimethylsiloxane-graphene oxide composite improving performance by ion beam irradiation
- 1.
SYSNO ASEP 0534250 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Polydimethylsiloxane-graphene oxide composite improving performance by ion beam irradiation Tvůrce(i) Cutroneo, Mariapompea (UJF-V) ORCID, RID, SAI
Havránek, Vladimír (UJF-V) RID, SAI, ORCID
Torrisi, Alfio (UJF-V) RID, ORCID
Macková, Anna (UJF-V) RID, ORCID, SAI
Malinský, Petr (UJF-V) RID, ORCID, SAI
Slepička, P. (CZ)
Sofer, Z. (CZ)
Torrisi, L. (IT)Celkový počet autorů 8 Zdroj.dok. Surface and Interface Analysis. - : Wiley - ISSN 0142-2421
Roč. 52, č. 12 (2020), s. 1156-1162Poč.str. 7 s. Forma vydání Tištěná - P Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova graphene oxide ; ion beam irradiation Vědní obor RIV CH - Jaderná a kvantová chemie, fotochemie Obor OECD Physical chemistry CEP GA19-02482S GA ČR - Grantová agentura ČR LM2015056 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy EF16_013/0001812 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Omezený přístup Institucionální podpora UJF-V - RVO:61389005 UT WOS 000578471400001 EID SCOPUS 85092380949 DOI 10.1002/sia.6882 Anotace A hybrid film consisting of graphene oxide covered with poly(dimethylsiloxane) was prepared via spin coater and followed by thermal annealing to improve the bond strength of the polymerized systems. Direct patterning on both graphene oxide and hybrid graphene oxide-poly(dimethylsiloxane) foils by ion microbeam was performed to induce localized reduction in the ion irradiated material. It is well established that the ion irradiation of graphene oxide induces modifications in its electrical, mechanical, and optical properties and disorder in the carbon crystal structure and defect production. The presence of poly(dimethylsiloxane) can be useful as it confers flexibility to the produced pattern and oxygen permeability from the graphene oxide surface. Rutherford backscattered spectroscopy and elastic recoil detection analysis were performed to evaluate the compositional changes in the composite. Atomic force microscopy studied the pattern fidelity. The electrical conductivity of the hybrid material was used to evaluate the changes induced during the proton irradiation of the material. Pracoviště Ústav jaderné fyziky Kontakt Markéta Sommerová, sommerova@ujf.cas.cz, Tel.: 266 173 228 Rok sběru 2021 Elektronická adresa https://doi.org/10.1002/sia.6882
Počet záznamů: 1