Thermal analysis of cesium hafnium chloride using DSC–TG under vacuum, nitrogen atmosphere, and in enclosed system
- 1.
SYSNO ASEP 0533015 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Thermal analysis of cesium hafnium chloride using DSC–TG under vacuum, nitrogen atmosphere, and in enclosed system Tvůrce(i) Král, Robert (FZU-D) RID, ORCID
Zemenová, Petra (FZU-D) RID, ORCID
Vaněček, Vojtěch (FZU-D) ORCID
Bystřický, Aleš (FZU-D)
Kohoutková, M. (CZ)
Jarý, Vítězslav (FZU-D) RID, ORCID
Kodama, S. (JP)
Kurosawa, S. (JP)
Yokota, Y. (JP)
Yoshikawa, A. (JP)
Nikl, Martin (FZU-D) RID, ORCID, SAICelkový počet autorů 11 Zdroj.dok. Journal of Thermal Analysis and Calorimetry. - : Akadémiai Kiadó - ISSN 1388-6150
Roč. 141, č. 3 (2020), s. 1101-1107Poč.str. 7 s. Jazyk dok. eng - angličtina Země vyd. HU - Maďarsko Klíč. slova Cesium hafnium chloride ; DSC–TG ; thermal stability ; scintillator Vědní obor RIV BM - Fyzika pevných látek a magnetismus Obor OECD Materials engineering CEP EF16_019/0000760 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy GJ18-17555Y GA ČR - Grantová agentura ČR Způsob publikování Omezený přístup Institucionální podpora FZU-D - RVO:68378271 UT WOS 000499820900004 EID SCOPUS 85076089834 DOI 10.1007/s10973-019-09087-7 Anotace This paper reports on the preparation of undoped Cs2HfCl6 and study of its thermal properties. The Cs2HfCl6 material was successfully synthesized from a cesium chloride and a hafnium chloride mixed together in stoichiometric ratio. The presence of only one crystalline phase of the Cs2HfCl6 in the material was confirmed by the X-ray diffraction analysis. The simultaneous DSC–TG thermal analysis of the synthesized material under nitrogen atmosphere, vacuum, and in enclosed system was performed. The Cs2HfCl6 decomposition and melting of CsCl–Cs2HfCl6 mixture under nitrogen and vacuum were observed. On the contrary, the DSC measurement of the cesium hafnium chloride in enclosed system showed only one endothermic peak related to the congruent melting point. Furthermore, the repeated DSC–TG measurements to investigate the materials’ stability in enclosed system were carried out as well.
Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2021 Elektronická adresa https://doi.org/10.1007/s10973-019-09087-7