Fatigue behavior of AW7075 aluminum alloy in ultra-high cycle fatigue region

  1. 1.
    SYSNO ASEP0523973
    Druh ASEPJ - Článek v odborném periodiku
    Zařazení RIVJ - Článek v odborném periodiku
    Poddruh JČlánek ve WOS
    NázevFatigue behavior of AW7075 aluminum alloy in ultra-high cycle fatigue region
    Tvůrce(i) Fintová, Stanislava (UFM-A) ORCID
    Kuběna, Ivo (UFM-A) RID, ORCID
    Trško, L. (SK)
    Horník, Vít (UFM-A)
    Kunz, Ludvík (UFM-A) RID, ORCID
    Celkový počet autorů5
    Číslo článku138922
    Zdroj.dok.Materials Science and Engineering A : Structural Materials: Properties, Microstructure and Processing. - : Elsevier - ISSN 0921-5093
    Roč. 774, FEB (2020)
    Poč.str.8 s.
    Jazyk dok.eng - angličtina
    Země vyd.CH - Švýcarsko
    Klíč. slovaprecipitate-free zones ; anodic-oxidation ; mechanisms ; performance ; damage ; life ; Fatigue ; Ultra-high cycle fatigue ; Fatigue crack initiation ; Fatigue damage ; aw7075
    Vědní obor RIVJG - Hutnictví, kovové materiály
    Obor OECDMaterials engineering
    CEPEF16_013/0001823 GA MŠk - Ministerstvo školství, mládeže a tělovýchovy
    Způsob publikováníOmezený přístup
    Institucionální podporaUFM-A - RVO:68081723
    UT WOS000514747200013
    EID SCOPUS85077674805
    DOI10.1016/j.msea.2020.138922
    AnotaceAdvanced electron microscopy methods were used with the aim to explain the differences in the response of strengthened AW 7075 T6511 aluminum alloy to fatigue loading at 5 Hz and 20 kHz. The shift of the S-N curve to higher number of cycles to fracture for the specimens tested at high frequency was experimentally determined. This effect is not connected with a change of the fatigue crack initiation mechanism and site from the surface to material interior. The absence of slip markings and cracking of primary intermetallic particles on the surface of cycled specimens were characteristic features. A difference in the dislocation density and dislocation arrangement in the vicinity of the fatigue crack initiation sites was shown to be the only observable effect. However, consistent with the strengthened structure of the alloy, no specific dislocation structure due to the cyclic loading was observed, regardless of the loading frequency and stress amplitude.