Fracture Resistance of 14Cr ODS Steel Exposed to a High Temperature Gas
- 1.
SYSNO ASEP 0506817 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Fracture Resistance of 14Cr ODS Steel Exposed to a High Temperature Gas Tvůrce(i) Hojná, A. (CZ)
Michalička, J. (CZ)
Hadraba, Hynek (UFM-A) RID, ORCID
Di Gabriele, F. (CZ)
Duchon, J. (CZ)
Rozumová, L. (CZ)
Husák, Roman (UFM-A)Celkový počet autorů 7 Číslo článku 560 Zdroj.dok. Metals. - : MDPI
Roč. 7, č. 12 (2017)Poč.str. 17 s. Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova ferritic alloys ; behavior ; microstructure ; mechanisms ; stability ; cr ; nanostructured steel ; thermal aging ; impact fracture ; microanalysis ; oxidation Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering CEP GA14-25246S GA ČR - Grantová agentura ČR LQ1601 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Open access Institucionální podpora UFM-A - RVO:68081723 UT WOS 000419184500045 EID SCOPUS 85038128447 DOI 10.3390/met7120560 Anotace This paper studies the impact fracture behavior of the 14%Cr Oxide Dispersion Strengthened (ODS) steel (ODM401) after high temperature exposures in helium and air in comparison to the as-received state. A steel bar was produced by mechanical alloying and hot-extrusion at 1150 degrees C. Further, it was cut into small specimens, which were consequently exposed to air or 99.9% helium in a furnace at 720 degrees C for 500 h. Impact energy transition curves are shifted towards higher temperatures after the gas exposures. The transition temperatures of the exposed states significantly increase in comparison to the as-received steel by about 40 degrees C in He and 60 degrees C in the air. Differences are discussed in terms of microstructure, surface and subsurface Scanning Electron Microscope (SEM) and Transmission Electron Microscope (TEM) observations. The embrittlement was explained as temperature and environmental effects resulting in a decrease of dislocation level, slight change of the particle composition and interface/grain boundary segregations, which consequently affected the nucleation of voids leading to the ductile fracture. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2020 Elektronická adresa https://www.mdpi.com/2075-4701/7/12/560/htm
Počet záznamů: 1