The investigation of an Al-Zr-Ti alloy prepared by spark plasma sintering of atomized powder
- 1.
SYSNO ASEP 0503785 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název The investigation of an Al-Zr-Ti alloy prepared by spark plasma sintering of atomized powder Tvůrce(i) Molnárová, O. (CZ)
Málek, P. (CZ)
Lukáč, František (UFP-V) ORCID
Chráska, Tomáš (UFP-V) RID, ORCID
Cinert, Jakub (UFP-V)Celkový počet autorů 5 Číslo článku 133486 Zdroj.dok. METAL 2017. 26th International Conference on Metallurgy and Materials. Conference Proceedings. - Ostrava : TANGER, 2017 - ISBN 978-80-87294-79-6 Rozsah stran 2017-january (2017), s. 1606-1612 Poč.str. 6 s. Forma vydání Nosič - C Akce 26th International Conference on Metallurgy and Materials Datum konání 24.05.2017 - 26.05.2017 Místo konání Brno Země CZ - Česká republika Typ akce EUR Jazyk dok. eng - angličtina Země vyd. CZ - Česká republika Klíč. slova Gas atomization ; High strength alloy ; Spark plasma sintering ; Thermal stability Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering CEP GA15-15609S GA ČR - Grantová agentura ČR Institucionální podpora UFP-V - RVO:61389021 UT WOS 000434346900259 EID SCOPUS 85043381358 Anotace The microstructure and mechanical properties of a powder metallurgical Al-Zr-Ti alloy was studied. Fine powder with a typical size below 50 ?m was prepared by gas atomization. The smallest powder particles with a diameter below 10 ?m exhibited a segregation free microstructure. Larger droplets were found to contain intermetallic particles rich in Zr and Ti. The gas atomized powder was consolidated by spark plasma sintering (SPS) at various temperatures ranging from 450 to 550 °C. During SPS the materials microstructure remained nearly unchanged and a fine grain size between 2 and 3 ?m was observed. All SPS samples exhibited a microhardness of around 90 HV. The annealing (1 h, 500 °C) of the sample sintered at the highest temperature (550 °C) resulted in a decrease of microhardness to 75 HV as a result of changes in the phase composition, the fine grain size was retained. Natural aging at room temperature was not observed. Pracoviště Ústav fyziky plazmatu Kontakt Vladimíra Kebza, kebza@ipp.cas.cz, Tel.: 266 052 975 Rok sběru 2020
Počet záznamů: 1