Interplay of slip and twinning in niobium single crystals compressed\nat 77 K
- 1.
SYSNO ASEP 0496930 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Interplay of slip and twinning in niobium single crystals compressed
at 77 KTvůrce(i) Gröger, Roman (UFM-A) RID, ORCID
Chlup, Zdeněk (UFM-A) RID, ORCID
Kuběnová, Tereza (UFM-A)
Kuběna, Ivo (UFM-A) RID, ORCIDCelkový počet autorů 4 Zdroj.dok. Journal of Materials Research. - : Springer - ISSN 0884-2914
Roč. 34, č. 2 (2019), s. 261-270Poč.str. 10 s. Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova niobium ; slip ; twinning ; 77 K ; plasticity Vědní obor RIV BM - Fyzika pevných látek a magnetismus Obor OECD Condensed matter physics (including formerly solid state physics, supercond.) CEP GA16-13797S GA ČR - Grantová agentura ČR LQ1601 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora UFM-A - RVO:68081723 UT WOS 000458506600004 EID SCOPUS 85056606228 DOI 10.1557/jmr.2018.398 Anotace High-purity niobium single crystals of five different orientations were compressed at 77 K to
2–4% plastic strain to investigate the mechanisms operative in the initial stage of yielding. The
crystals deformed in the direction close to the [001] axis exhibit predominant slip on the highstressed
(101) and a much lower stressed ð0 11Þ plane. The expected slip on the ð 101Þ plane is
nearly homogeneously distributed with only a few sharp slip traces corresponding to localized
slip. The samples compressed along center-triangle orientations and those close to the
½011 ½ 111 edge deform predominantly by twinning on {112}h111i systems with some
contribution from slip on the ð 101Þ½ 1 1 1 system with the highest Schmid factor. A majority of
twins exhibit internal contrast due to alternating slip on ð 101Þ and ð0 11Þ planes. No slip traces are
observed in the matrix adjacent to the twin, which implies that twin boundaries are impenetrable
obstacles for the motion of dislocations.Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2019