Initiation and growth of short fatigue cracks in austenitic Sanicro 25 steel
- 1.
SYSNO ASEP 0492026 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Initiation and growth of short fatigue cracks in austenitic Sanicro 25 steel Tvůrce(i) Mazánová, Veronika (UFM-A)
Polák, Jaroslav (UFM-A) RID, ORCIDCelkový počet autorů 2 Zdroj.dok. Fatigue and Fracture of Engineering Materials and Structures - ISSN 8756-758X
Roč. 41, č. 7 (2018), s. 1529-1545Poč.str. 17 s. Forma vydání Tištěná - P Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova austenitic steel ; crack growth ; crack growth coefficient ; crack initiation ; EBSD ; equivalent crack Vědní obor RIV JL - Únava materiálu a lomová mechanika Obor OECD Audio engineering, reliability analysis CEP LM2015069 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy LQ1601 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy LM2015069 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy GA15-08826S GA ČR - Grantová agentura ČR GA13-23652S GA ČR - Grantová agentura ČR Institucionální podpora UFM-A - RVO:68081723 UT WOS 000434273100007 DOI https://doi.org/10.1111/ffe.12794 Anotace Austenitic heat‐resistant stainless steel Sanicro 25, often used in energy production
installations, was cyclically strained at room temperature, and initiation
and growth of short fatigue cracks have been studied. Cylindrical specimens
with pre‐existing shallow notch were cyclically strained under constant total
strain amplitudes, while the surface relief, crack initiation, and short crack
growth were observed, in‐situ, using optical and electron microscopes.
Persistent slip markings were found to be the principal locations where natural
fatigue cracks initiated. The character of the crack paths of short cracks was
studied using SEM and EBSD techniques. The results exhibit prevailing
transgranular crack growth, ie, along the persistent slip markings within the
grains. The growth of the largest cracks in the central part of the shallow notch
was measured for different applied strain amplitudes. Because the coalescence
of initiated cracks plays a significant role during crack growth, the use of the
“equivalent crack” concept gives adequate results in the description of the crack
growth rate. The crack growth law of short cracks was established and
compared with the Manson‐Coffin law of the material.Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2019