Fatigue crack initiation and growth in 43Fe-25Ni-22.5Cr austenitic steel at a temperature of 700 °C

  1. 1.
    SYSNO ASEP0492025
    Druh ASEPJ - Článek v odborném periodiku
    Zařazení RIVJ - Článek v odborném periodiku
    Poddruh JČlánek ve WOS
    NázevFatigue crack initiation and growth in 43Fe-25Ni-22.5Cr austenitic steel at a temperature of 700 °C
    Tvůrce(i) Mazánová, Veronika (UFM-A)
    Heczko, Milan (UFM-A)
    Polák, Jaroslav (UFM-A) RID
    Celkový počet autorů3
    Zdroj.dok.International Journal of Fatigue. - : Elsevier - ISSN 0142-1123
    Roč. 114, SEP (2018), s. 11-21
    Poč.str.11 s.
    Forma vydáníTištěná - P
    Jazyk dok.eng - angličtina
    Země vyd.GB - Velká Británie
    Klíč. slovaHigh temperature fatigue ; oxidation ; crack initiation ; crack growth ; Sanicro 25
    Vědní obor RIVJL - Únava materiálu a lomová mechanika
    Obor OECDAudio engineering, reliability analysis
    CEPLM2015069 GA MŠk - Ministerstvo školství, mládeže a tělovýchovy
    LQ1601 GA MŠk - Ministerstvo školství, mládeže a tělovýchovy
    GA13-23652S GA ČR - Grantová agentura ČR
    GA15-08826S GA ČR - Grantová agentura ČR
    EF16_027/0008056 GA MŠk - Ministerstvo školství, mládeže a tělovýchovy
    Institucionální podporaUFM-A - RVO:68081723
    UT WOS000441487100002
    EID SCOPUS85047597808
    DOI10.1016/j.ijfatigue.2018.04.033
    AnotaceCrack initiation and short crack growth in highly-alloyed austenitic steel Sanicro 25 cyclically strained at atemperature of 700 °C has been studied. Specimens cycled to 10% of the fatigue life and to the fracture wereinspected using scanning electron microscopy and electron backscatter diffraction. On the surface, thin lamellaewere extracted site-specifically by focused ion beam and then they were further characterized by high spatialresolution scanning transmission electron microscopy and energy dispersive X-ray spectroscopy. The preferentialoxidation of grain boundaries was found to play a principal role in the initiation of multiple cracks. The oxidescale was analysed to show the distribution of individual elements during crack initiation and growth. Two typesof crack paths were observed: intergranular due to the oxidation and transgranular accompanied by a cyclicplastic zone. Cracks preferentially initiated at the grain boundaries perpendicular to the stress axis and propa-gated in the bulk of the material. The role of the oxidation in high temperature fatigue crack initiation isdiscussed as well as the mechanisms of the crack initiation and growth.