Fatigue crack initiation and growth in 43Fe-25Ni-22.5Cr austenitic steel at a temperature of 700 °C
- 1.
SYSNO ASEP 0492025 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Fatigue crack initiation and growth in 43Fe-25Ni-22.5Cr austenitic steel at a temperature of 700 °C Tvůrce(i) Mazánová, Veronika (UFM-A)
Heczko, Milan (UFM-A) ORCID
Polák, Jaroslav (UFM-A) RID, ORCIDCelkový počet autorů 3 Zdroj.dok. International Journal of Fatigue. - : Elsevier - ISSN 0142-1123
Roč. 114, SEP (2018), s. 11-21Poč.str. 11 s. Forma vydání Tištěná - P Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova High temperature fatigue ; oxidation ; crack initiation ; crack growth ; Sanicro 25 Vědní obor RIV JL - Únava materiálu a lomová mechanika Obor OECD Audio engineering, reliability analysis CEP LM2015069 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy LQ1601 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy GA13-23652S GA ČR - Grantová agentura ČR GA15-08826S GA ČR - Grantová agentura ČR EF16_027/0008056 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora UFM-A - RVO:68081723 UT WOS 000441487100002 EID SCOPUS 85047597808 DOI 10.1016/j.ijfatigue.2018.04.033 Anotace Crack initiation and short crack growth in highly-alloyed austenitic steel Sanicro 25 cyclically strained at atemperature of 700 °C has been studied. Specimens cycled to 10% of the fatigue life and to the fracture wereinspected using scanning electron microscopy and electron backscatter diffraction. On the surface, thin lamellaewere extracted site-specifically by focused ion beam and then they were further characterized by high spatialresolution scanning transmission electron microscopy and energy dispersive X-ray spectroscopy. The preferentialoxidation of grain boundaries was found to play a principal role in the initiation of multiple cracks. The oxidescale was analysed to show the distribution of individual elements during crack initiation and growth. Two typesof crack paths were observed: intergranular due to the oxidation and transgranular accompanied by a cyclicplastic zone. Cracks preferentially initiated at the grain boundaries perpendicular to the stress axis and propa-gated in the bulk of the material. The role of the oxidation in high temperature fatigue crack initiation isdiscussed as well as the mechanisms of the crack initiation and growth. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2019
Počet záznamů: 1