Initiation of fatigue cracks and lifetime of Ni-base superalloys at high mean stress and temperature
- 1.
SYSNO ASEP 0483642 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Initiation of fatigue cracks and lifetime of Ni-base superalloys at high mean stress and temperature Tvůrce(i) Kunz, Ludvík (UFM-A) RID, ORCID
Horník, Vít (UFM-A)
Hutař, Pavel (UFM-A) RID, ORCID
Fintová, Stanislava (UFM-A) ORCIDCelkový počet autorů 4 Zdroj.dok. 3RD INTERNATIONAL SYMPOSIUM ON FATIGUE DESIGN AND MATERIAL DEFECTS (FDMD 2017). - Amsterdam : Elsevier, 2017 / Beretta S. ; Foletti S. ; Nicoletto G. ; Tovo R. - ISSN 2452-3216 Rozsah stran s. 44-49 Poč.str. 6 s. Forma vydání Online - E Akce FDMD 2017 - International Symposium on Fatigue Design and Material Defects /3./ Datum konání 19.09.2017 - 22.09.2017 Místo konání Lecco Země IT - Itálie Typ akce WRD Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova IN 713LC ; MAR-M247 ; creep/fatigue loading ; time to fracture Vědní obor RIV JL - Únava materiálu a lomová mechanika Obor OECD Audio engineering, reliability analysis CEP EG15_019/0004399 GA MPO - Ministerstvo průmyslu a obchodu Institucionální podpora UFM-A - RVO:68081723 UT WOS 000452909100007 DOI 10.1016/j.prostr.2017.11.059 Anotace The effect of high-frequency cycling (120 Hz) superimposed on high tensile mean stress on a lifetime of cast Ni-base superalloys IN 713LC at 800 °C and MAR-M 247 at 900 °C was investigated. It has been found that both the alloys exhibit qualitatively similar behavior in creep/fatigue loading conditions. Superposition of small stress amplitudes on the tensile mean stress does not influence the time to fracture until the stress amplitude reaches a threshold value, which is dependent on the mean stress. The higher the mean stress the higher is the stress amplitude threshold value. The observed creep/fatigue behavior is governed by two mechanisms: (a) formation and growth of intergranular cracks by creep mechanism (b) initiation and growth of fatigue cracks from the intergranular creep cracks. The casting defects do not play any important role as regards the lifetime under investigated loading conditions. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2019
Počet záznamů: 1