The Application of Miniaturized Three-Point-Bend Specimens for Determination of the Reference Temperature of A533 Cl.1 Steel
- 1.
SYSNO ASEP 0481466 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název The Application of Miniaturized Three-Point-Bend Specimens for Determination of the Reference Temperature of A533 Cl.1 Steel Tvůrce(i) Stratil, Luděk (UFM-A) ORCID
Šiška, Filip (UFM-A) RID, ORCID
Dlouhý, Ivo (UFM-A) RID, ORCID
Serrano, M. (ES)Celkový počet autorů 4 Číslo článku 041410 Zdroj.dok. Journal of Pressure Vessel Technology-Transactions of the Asme - ISSN 0094-9930
Roč. 139, č. 4 (2017)Poč.str. 6 s. Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova fracture toughness ; Master Curve ; the reference temperature ; JRQ steel ; miniaturized specimens Vědní obor RIV JL - Únava materiálu a lomová mechanika Obor OECD Audio engineering, reliability analysis CEP GJ15-21292Y GA ČR - Grantová agentura ČR ED1.1.00/02.0068 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora UFM-A - RVO:68081723 UT WOS 000403902100022 EID SCOPUS 85019699188 DOI 10.1115/1.4036532 Anotace This contribution deals with the determination of the reference temperature of JRQ steel using miniaturized
specimens. The dimensions of the miniaturized specimens used were 3 × 4 × 27 mm (thickness × width ×
length). This specimen type allows utilizing a limited amount of test material or the broken halves of pre-cracked
Charpy or larger specimens. The test material comes from the broken halves of 0.5T SE(B) specimens
previously tested for the determination of the reference temperature at Ciemat, Madrid. The fracture toughness
tests were performed in the transition region of the steel according to the recommendations of the standard
ASTM E1921 and according to Wallin’s recommended temperature range of miniaturized specimens. The
reference temperature of the Master Curve was very similar to the ones obtained from three-point-bend
specimens of sizes 0.2T, 0.4T and 0.5T. The results obtained confirm a necessity to conduct tests at low
temperatures and to test a sufficient number of specimens in order to generate enough valid data for the
determination of the reference temperature.Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2018