Fracture behaviour of the 14Cr ODS steel exposed to helium and liquid lead
- 1.
SYSNO ASEP 0480409 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Fracture behaviour of the 14Cr ODS steel exposed to helium and liquid lead Tvůrce(i) Hojná, A. (CZ)
Di Gabriele, F. (CZ)
Hadraba, Hynek (UFM-A) RID, ORCID
Husák, Roman (UFM-A)
Kuběna, Ivo (UFM-A) RID, ORCID
Rozumová, L. (CZ)
Bublíková, P. (CZ)
Kalivodová, J. (CZ)
Matějíček, Jiří (UFP-V) RID, ORCIDCelkový počet autorů 9 Zdroj.dok. Journal of Nuclear Materials. - : Elsevier - ISSN 0022-3115
Roč. 490, JUL (2017), s. 143-154Poč.str. 12 s. Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova Impact fracture ; Microanalysis ; Nanostructured steel ; Oxidation ; Thermal ageing Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering Vědní obor RIV – spolupráce Ústav fyziky plazmatu - Hutnictví, kovové materiály CEP GA14-25246S GA ČR - Grantová agentura ČR GA14-12837S GA ČR - Grantová agentura ČR LQ1601 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora UFM-A - RVO:68081723 ; UFP-V - RVO:61389021 UT WOS 000403132300017 EID SCOPUS 85018463374 DOI 10.1016/j.jnucmat.2017.03.049 Anotace This work describes the fracture behaviour of the 14Cr ODS steel produced by mechanical alloying process, after high temperature exposures. Small specimens were exposed to helium gas in a furnace at 720 degrees C for 500 h. Another set of specimens was exposed to flowing liquid lead in the COLONRI II loop at 650 degrees C for 1000 h. All specimens were tested for the impact and tensile behaviour. The impact test results are compared to other sets of specimens in the as received state and after isothermal annealing at 650 degrees C for 1000 h. The impact curves of the exposed materials showed positive shifts on the transition temperature. While the upper shelf value did not change in the Pb exposed ODS steel, it significantly increased in the He exposed one. The differences are discussed in terms of surface and subsurface microscopy observation. The embrittlement can be explained as the effect of a slight change in the grain boundary and size distribution combined with the depletion of sub-surface region from alloying elements forming oxide scale on the surface. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2018