HYDROGENATION OF CHOSEN MgMXN INTERMETALLICS (X=Al, Ga, In, Si, Sn)
- 1.
SYSNO ASEP 0473834 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název HYDROGENATION OF CHOSEN MgMXN INTERMETALLICS (X=Al, Ga, In, Si, Sn) Tvůrce(i) Čermák, Jiří (UFM-A) RID, ORCID
Král, Lubomír (UFM-A) RID, ORCID
Roupcová, Pavla (UFM-A) RID, ORCIDCelkový počet autorů 3 Zdroj.dok. NANOCON 2016. 8th International Conference on Nanomaterials - Research and Application. Conference Proceedings. - Ostrava : Tanger, 2017 - ISBN 978-80-87294-71-0 Rozsah stran s. 715-720 Poč.str. 6 s. Forma vydání Nosič - C Akce NANOCON 2016. International Conference on Nanomaterials - Research and Application /8./ Datum konání 19.10.2016 - 21.10.2016 Místo konání Brno Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CZ - Česká republika Klíč. slova Hydrogen ; hydrogen storage ; Mg alloys ; hydrogen solubility ; MgH2 Vědní obor RIV BJ - Termodynamika Obor OECD Thermodynamics CEP LQ1601 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora UFM-A - RVO:68081723 UT WOS 000410656100124 Anotace Hydrogen sorption in chosen intermetallics MgmXn (Mg17Al12 , Mg2Ga, mixture of beta-Mg-In phases, Mg2Si and Mg2Sn) formed by magnesium and elements from the 13 th (X: Al, Ga, In) and 14 th (X: Si, Sn) groups was studied between the room temperature and T = 350 °C. Hydrogen pressure p varied from 10-3 MPa to 6 MPa.
Hydrogen solubility in alpha phase (solid solution of hydrogen in MgmXn before the hydride phase was nucleated) was close to hydrogen solubility in pure Mg. Concentration cH of hydrogen solved in Mg m X n depended linearly on pressure p , dependence of cH on temperature T was relatively weak. MgH2 was the main hydrogen storage phase in all the compounds MgmXn . Nucleation of MgH2 at 350 °C was observed at pressure above approximately 1 MPa in Mg17Al12 and above 2 Ma in other compounds. Maximum values of c H in hydride-containing compounds MgmXn detected at T = 350 °C depended on the stability of MgmXn .Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2018
Počet záznamů: 1