HYDROGENATION PROPERTIES OF BALL-MILLED Mg-Ti-C-Zr COMPOSITE

  1. 1.
    SYSNO ASEP0468223
    Druh ASEPC - Konferenční příspěvek (mezinárodní konf.)
    Zařazení RIVD - Článek ve sborníku
    NázevHYDROGENATION PROPERTIES OF BALL-MILLED Mg-Ti-C-Zr COMPOSITE
    Tvůrce(i) Král, Lubomír (UFM-A) RID, ORCID
    Čermák, Jiří (UFM-A) RID, ORCID
    Roupcová, Pavla (UFM-A) RID, ORCID
    Celkový počet autorů3
    Zdroj.dok.METAL 2016: 25th International Conference on Metallurgy and Materials. - Ostrava : Tanger Ltd., 2016 - ISBN 978-80-87294-67-3
    Rozsah strans. 1445-1449
    Poč.str.5 s.
    Forma vydáníNosič - C
    AkceMETAL 2016 - Anniversary International Conference on Metallurgy and Materials /25./
    Datum konání25.05.2016 - 27.05.2016
    Místo konáníBrno
    ZeměCZ - Česká republika
    Typ akceWRD
    Jazyk dok.eng - angličtina
    Země vyd.CZ - Česká republika
    Klíč. slovahydrides ; hydrogen storage ; Mg-alloys
    Vědní obor RIVJJ - Ostatní materiály
    CEPED1.1.00/02.0068 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy
    Institucionální podporaUFM-A - RVO:68081723
    UT WOS000391251200236
    EID SCOPUS85010817740
    AnotaceThe hydrogen storage properties of ball-milled Mg-Ti-Zr-C composite (1.8 wt.% Ti, 1.9 wt.% Zr and 0.2 wt.% C) were investigated. It has been previously shown, that the addition of Ti, Zr and C improved its storage properties. This beneficial effect of additives upon hydrogen storage properties can be explained by catalysis by the particles rich in Ti or Zr located on the surface of Mg grains. They provide effective pathways for the hydrogen diffusion into the MgH2. The morphological and microstructural characteristics were investigated by scanning electron microscopy and by X-ray diffraction. The hydrogen sorption was measured by Sieverts method using Setaram PCT-Pro device. In this paper, sorption behaviour of the composite after ball-milling and after aging on the air was compared. The ball-milled composite adsorbed 3.5 wt.% H2 within 10 min at 623 K. However, hydrogen storage capacity of the composite aged on the air for 7 months remarkably decreased: The aged composite adsorbed within 10 min only 2 wt.% H2 at 623 K and the sorption capacity decreased from 4.7 wt.% H2 to 2.1 wt.% H2.
    PracovištěÚstav fyziky materiálu
    KontaktYvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485
    Rok sběru2017
Počet záznamů: 1  

  Tyto stránky využívají soubory cookies, které usnadňují jejich prohlížení. Další informace o tom jak používáme cookies.