The formation of silver metal nanoparticles by ion implantation in silicate glasses
- 1.
SYSNO ASEP 0459131 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název The formation of silver metal nanoparticles by ion implantation in silicate glasses Tvůrce(i) Vytykačová, S. (CZ)
Švecová, B. (CZ)
Nekvindová, P. (CZ)
Špirková, J. (CZ)
Macková, Anna (UJF-V) RID, ORCID, SAI
Mikšová, Romana (UJF-V) RID, ORCID, SAI
Bottger, R. (DE)Celkový počet autorů 7 Zdroj.dok. Nuclear Instruments & Methods in Physics Research Section B. - : Elsevier - ISSN 0168-583X
Roč. 371, MAR (2016), s. 245-255Poč.str. 6 s. Forma vydání Tištěná - P Akce 22nd International conference on Ion Beam Analysis (IBA) Datum konání 14.06.2015 - 19.06.2015 Místo konání Opatija Země HR - Chorvatsko Typ akce WRD Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova silicate glasses ; silver nanoparticles ; ion implantation Vědní obor RIV BG - Jaderná, atomová a mol. fyzika, urychlovače CEP LM2011019 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy GA15-01602S GA ČR - Grantová agentura ČR Institucionální podpora UJF-V - RVO:61389005 UT WOS 000373412000047 EID SCOPUS 84960290680 DOI 10.1016/j.nimb.2015.10.016 Anotace t has been shown that glasses containing silver metal nanoparticles are promising photonics materials for the fabrication of all-optical components. The resulting optical properties of the nanocomposite glasses depend on the composition and structure of the glass, as well as on the type of metal ion implanted and the experimental procedures involved. The main aim of this article was to study the influence of the conditions of the ion implantation and the composition of the glass on the formation of metal nanoparticles in such glasses.
Four various types of silicate glasses were implanted with Ag+ ions with different energy (330 keV, 1.2 MeV and 1.7 MeV), with the fluence being kept constant (1 x 10(16) ions cm(-2)). The as-implanted samples were annealed at 600 degrees C for 1 h. The samples were characterised in terms of: the nucleation of metal nanoparticles (linear optical absorption), the migration of silver through the glass matrix during the implantation and post-implantation annealing (Rutherford backscattering spectroscopy), and the oxidation state of silver (photoluminescence in the visible region).Pracoviště Ústav jaderné fyziky Kontakt Markéta Sommerová, sommerova@ujf.cas.cz, Tel.: 266 173 228 Rok sběru 2017