Effect of high-flux H/He plasma exposure on tungsten damage due to transient heat loads
- 1.
SYSNO ASEP 0444972 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Effect of high-flux H/He plasma exposure on tungsten damage due to transient heat loads Tvůrce(i) De Temmerman, G. (NL)
Morgan, T.W. (NL)
van Eden, G.G. (NL)
de Kruif, T. (NL)
Wirtz, M. (DE)
Matějíček, Jiří (UFP-V) RID, ORCID
Chráska, Tomáš (UFP-V) RID, ORCID
Pitts, R.A. (FR)
Wright, G.M. (US)Zdroj.dok. Journal of Nuclear Materials. - : Elsevier - ISSN 0022-3115
Roč. 463, August (2015), s. 198-201Poč.str. 4 s. Forma vydání Tištěná - P Akce PLASMA-SURFACE INTERACTIONS 21: International Conference on Plasma-Surface Interactions in Controlled Fusion Devices Datum konání 26.05.2014-30.05.2014 Místo konání Kanazawa Země JP - Japonsko Typ akce WRD Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova plasma-facing components ; tungsten ; hydrogen ; helium ; ELM Vědní obor RIV JF - Jaderná energetika Obor OECD Nuclear related engineering CEP GA14-12837S GA ČR - Grantová agentura ČR Institucionální podpora UFP-V - RVO:61389021 UT WOS 000358467200033 EID SCOPUS 84937705153 DOI 10.1016/j.jnucmat.2014.09.075 Anotace The thermal shock behaviour of tungsten exposed to high-flux plasma is studied using a high-power laser. The cases of laser-only, sequential laser and hydrogen (H) plasma and simultaneous laser plus H plasma exposure are studied. H plasma exposure leads to an embrittlement of the material and the appearance of a crack network originating from the centre of the laser spot. Under simultaneous loading, significant surface melting is observed. In general, H plasma exposure lowers the heat flux parameter (FHF) for the onset of surface melting by _25%. In the case of He-modified (fuzzy) surfaces, strong surface deformations are observed already after 1000 laser pulses at moderate FHF = 19MJ m_2 s_1/2, and a dense network of fine cracks is observed. These results indicate that high-fluence ITER-like plasma exposure influences the thermal shock properties of tungsten, lowering the permissible transient energy density beyond which macroscopic surface modifications begin to occur. Pracoviště Ústav fyziky plazmatu Kontakt Vladimíra Kebza, kebza@ipp.cas.cz, Tel.: 266 052 975 Rok sběru 2016
Počet záznamů: 1