Spark Plasma Sintering of Multilayer Ceramics – Case Study of Al2O3 - Mg(Ca)TiO3 Sandwich
- 1.
SYSNO ASEP 0428489 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Spark Plasma Sintering of Multilayer Ceramics – Case Study of Al2O3 - Mg(Ca)TiO3 Sandwich Tvůrce(i) Ctibor, Pavel (UFP-V) RID, ORCID
Kubatík, Tomáš František (UFP-V)
Chráska, Pavel (UFP-V) RIDZdroj.dok. Key Engineering Materials, 606. - Zurich : Trans Tech Publications Ltd, 2014 / Haušíld P. ; Materna A. ; Vilémová M. - ISSN 1662-9795 Rozsah stran s. 205-208 Poč.str. 4 s. Forma vydání Tištěná - P Akce International Conference on Local Mechanical Properties, LMP 2013/10./ Datum konání 06.11.2013-08.11.2013 Místo konání Kutná Hora Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova Al2O3 - Mg(Ca)TiO3 ; Sandwich ceramics ; Spark Plasma Sintering Vědní obor RIV JH - Keramika, žáruvzdorné materiály a skla Institucionální podpora UFP-V - RVO:61389021 Anotace Spark plasma sintering enables very rapid fabrication of bulk ceramic materials. Suitability of this technique for preparing of multilayer ceramic discs is up to now relatively seldom reported.Our work is focused on a bi-layered disc consisting of thick Al2O3 layer and comparably thick Mg(Ca)TiO3 (MCT) layer sintered in one run.Al2O3 powder was nanometric (less than 40 nm) and composed of the hexagonal α-phase whereas MCT is a solid solution of two orthorombic perovskites.Pre-sintered and crushed MCT powder was coarser than alumina, up to 125 μm.The purpose of this material combination was creating of dielectric sandwich consisting of capacitor MCT material and resistor nanoalumina material.Spark plasma sintering run was done at 1200 °C, using pressure 80 MPa and dwell time only 2min.Resulting sandwich was subjected to microstructural observations and cross sectional measurement of microhardness.On the border between Al2O3 and MCT the microhardness was higher than in MCT but has Pracoviště Ústav fyziky plazmatu Kontakt Vladimíra Kebza, kebza@ipp.cas.cz, Tel.: 266 052 975 Rok sběru 2015
Počet záznamů: 1