Effect of Cyclic Heat Treatment on Cast Structure of TiAl Alloy

    1.
    SYSNO ASEP0397330
    Druh ASEPC - Konferenční příspěvek (mezinárodní konf.)
    Zařazení RIVD - Článek ve sborníku
    NázevEffect of Cyclic Heat Treatment on Cast Structure of TiAl Alloy
    Tvůrce(i) Petrenec, Martin (UFM-A)
    Vraspírová, E. (CZ)
    Němec, K. (CZ)
    Heczko, Milan (UFM-A) ORCID
    Celkový počet autorů4
    Zdroj.dok.Local Mechanical Properties IX. - Zurich : Trans Tech Publications, 2014 / Pešek L. ; Zubko P. - ISSN 1013-9826 - ISBN 978-3-03785-876-9
    Rozsah strans. 222-225
    Poč.str.4 s.
    Forma vydáníTištěná - P
    AkceLMP 2012 International Conference on Local Mechanical Properties /9./
    Datum konání07.11.2012-09.11.2012
    Místo konáníLevoča
    ZeměSK - Slovensko
    Typ akceWRD
    Jazyk dok.eng - angličtina
    Země vyd.CH - Švýcarsko
    Klíč. slovaTiAl alloy ; cyclic heat treatment ; refined cast structure ; discontinuous coarsening ; microhardness
    Vědní obor RIVJL - Únava materiálu a lomová mechanika
    CEPGAP107/11/0704 GA ČR - Grantová agentura ČR
    Institucionální podporaUFM-A - RVO:68081723
    UT WOS000336633500054
    EID SCOPUS84885788125
    DOI10.4028/www.scientific.net/KEM.586.222
    AnotaceThe subject of the article is focused on the refining of the cast structure of gamma TiAl-2Nb alloy using cyclic heat treatment and on the analysis of the grain refining mechanism. Microstructure evolution after applied cycles of heat treatment was characterized using light, laser and electron microscopy and using microhardness tests. Application of five heat treatment cycles during which two phase transformations (eutectoid and alpha-recrystallization reactions) repeatedly took place resulted in refining of the cast columnar structure. The mean grain-lamellar colony size 512 micrometers was transformed to fully lamellar structure containing gamma and alpha2 phases having the mean grain size 229 micrometers. Lamellae thickness of gamma was not changed while the thickness of alpha2 phase decreased to 78 nm. Refining of alpha2 phase resulted in the increase of the microhardness by 20 %. The recrystallized cast structure obtained by cyclic heat treatment and the knowledge on the mechanisms of the refining the structure were compared and discussed with the literature data.
    PracovištěÚstav fyziky materiálu
    KontaktYvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485
    Rok sběru2015
Počet záznamů: 1  

  Tyto stránky využívají soubory cookies, které usnadňují jejich prohlížení. Další informace o tom jak používáme cookies.

Přijmout všeNastaveníOdmítnout vše