Surface DBD for deposition of the PEO-like plasma polymers
- 1.
SYSNO ASEP 0376614 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Surface DBD for deposition of the PEO-like plasma polymers Tvůrce(i) Gordeev, Ivan (UFP-V)
Šimek, Milan (UFP-V) RID, ORCID
Prukner, Václav (UFP-V) RID, ORCID
Choukourov, A. (CZ)
Biederman, H. (CZ)Celkový počet autorů 5 Zdroj.dok. Plasma Processes and Polymers. - : Wiley - ISSN 1612-8850
Roč. 9, č. 1 (2012), s. 83-89Poč.str. 7 s. Forma vydání web - web Jazyk dok. eng - angličtina Země vyd. DE - Německo Klíč. slova AC barrier discharges ; surface discharges ; plasma polymers ; poly(ethylene oxide) (PEO) ; UV-vis spectroscopy Vědní obor RIV BL - Fyzika plazmatu a výboje v plynech CEP GD104/09/H080 GA ČR - Grantová agentura ČR CEZ AV0Z20430508 - UFP-V (2005-2011) UT WOS 000298842100011 DOI 10.1002/ppap.201100051 Anotace This work investigates the possibility to prepare PEO-like plasma polymers by using an AC surface dielectric barrier discharge in argon with admixtures of di(ethylene glycol) monovinyl ether vapours at atmospheric pressure. The surface discharge was driven in an amplitude-modulated regime with a driving AC frequency of 5 kHz with a variable discharge duty cycle of 0,2-0,8. Deposition of plasma polymers was tested for variable argon flow rate of 0,5-2 slm and for various distances between the discharge electrode surface and deposition substrates. The measurements of electro-optical discharge characteristics and infrared analysis of deposited films were performed to fix suitable deposition conditions. Best retention of PEO-like character was obtained for the following conditions: the distance between substrates and discharge surface of 3 mm, argon flow rate of 1 slm, excitation AC high voltage of 2,2 kV (peak-to-peak) and discharge duty cycle of 0,4. Pracoviště Ústav fyziky plazmatu Kontakt Vladimíra Kebza, kebza@ipp.cas.cz, Tel.: 266 052 975 Rok sběru 2013 Elektronická adresa http://onlinelibrary.wiley.com/doi/10.1002/ppap.201100051/pdf
Počet záznamů: 1