Apparent Fracture Toughness of Low-carbon Steel CSN 411353 as Related to Stress Corrosion Cracks
- 1.
SYSNO ASEP 0361566 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Apparent Fracture Toughness of Low-carbon Steel CSN 411353 as Related to Stress Corrosion Cracks Tvůrce(i) Gajdoš, Lubomír (UTAM-F) RID, SAI
Šperl, Martin (UTAM-F) RID, SAI
Siegl, J. (CZ)Celkový počet autorů 3 Zdroj.dok. Materials & Design. - : Elsevier - ISSN 0261-3069
Roč. 32, 8/9 (2011), s. 4348-4353Poč.str. 6 s. Forma vydání on-line www - on-line www Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova corrosion ; fracture ; fractography Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP GAP105/10/2052 GA ČR - Grantová agentura ČR GPP105/10/P555 GA ČR - Grantová agentura ČR CEZ AV0Z20710524 - UTAM-F (2005-2011) UT WOS 000292621000028 EID SCOPUS 79957791057 DOI https://doi.org/10.1016/j.matdes.2011.04.001 Anotace The occurrence of cracks in structural components indicates a certain threat to their reliable operation, because these cracks can grow during operation and reach critical sizes, leading to fracture. The fracture resistance of a structural component is given by the fracture toughness of the material, determined on standardized specimens with a precycled fatigue crack, and the constraint. The fracture toughness itself depends also on the environment. There is enough evidence that in the conditions of the environment assisted cracking the fracture toughness can be significantly reduced by hydrogen mechanism. Our research results have confirmed this and have demonstrated a considerable reduction in the stress corrosion fracture toughness as compared to that related to fatigue cracks. This should be taken into account when assessing the integrity of structural components with stress corrosion cracks. Pracoviště Ústav teoretické a aplikované mechaniky Kontakt Kulawiecová Kateřina, kulawiecova@itam.cas.cz, Tel.: 225 443 285 Rok sběru 2012
Počet záznamů: 1