Počet záznamů: 1
Analysis of fatigue crack initiation in cycled austempered ductile cast irons
- 1.
SYSNO ASEP 0355182 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Analysis of fatigue crack initiation in cycled austempered ductile cast irons Tvůrce(i) Petrenec, Martin (UFM-A)
Beran, Přemysl (UJF-V) RID, ORCID, SAI
Dluhoš, J. (CZ)
Zouhar, Michal (UFM-A)
Ševčík, Martin (UFM-A) RIDZdroj.dok. Procedia Engineering. - Amsterdam : Elsevier BV
Roč. 2, č. 1 (2010), s. 2337-2346Poč.str. 10 s. Akce Fatigue 2010 Datum konání 06.06.2010-11.06.2010 Místo konání Praha Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova Low cycle fatigue ; ADI ; Finite element modelling ; Neutron diffraction Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP GAP108/10/2371 GA ČR - Grantová agentura ČR GD106/09/H035 GA ČR - Grantová agentura ČR CEZ AV0Z20410507 - UFM-A (2005-2011) AV0Z10480505 - UJF-V (2005-2011) UT WOS 000278762900248 DOI 10.1016/j.proeng.2010.03.250 Anotace Interrupted total strain controlled tests have been performed on cylindrical specimens of austempered ductile cast iron (ADI) with the aim to study fatigue crack initiation and provide the fine numerical simulations at temperatures 23 °C and–45 °C. The systematic observation of the same places on surface specimen by SEM was done in interrupted low cycle fatigue test. Fatigue cracks initiated preferably from persistent slip markings at the interface of graphite nodule and the ausferrite matrix and places without visible graphite nodule. To prove this assumption the numerical simulations were performed in order to study this situation in more details. The numerical analyses presented here helped to better understanding of the experimentally observed processes in the fatigued ADI. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2011
Počet záznamů: 1