Facile Conversion of Electrospun TiO2 into Titanium Nitride/Oxynitride Fibers
- 1.
SYSNO ASEP 0350911 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Facile Conversion of Electrospun TiO2 into Titanium Nitride/Oxynitride Fibers Tvůrce(i) Zukalová, Markéta (UFCH-W) RID, SAI, ORCID
Procházka, Jan (UFCH-W)
Bastl, Zdeněk (UFCH-W) RID, ORCID
Duchoslav, J. (CZ)
Rubáček, L. (CZ)
Havlíček, D. (CZ)
Kavan, Ladislav (UFCH-W) RID, ORCIDZdroj.dok. Chemistry of Materials. - : American Chemical Society - ISSN 0897-4756
Roč. 22, č. 13 (2010), s. 4045-4055Poč.str. 11 s. Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova visible-light photocatalysis ; nitrogen doped TiO2 ; thin films Vědní obor RIV CG - Elektrochemie CEP LC510 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy OC09048 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy IAA400400804 GA AV ČR - Akademie věd KAN200100801 GA AV ČR - Akademie věd CEZ AV0Z40400503 - UFCH-W (2005-2011) UT WOS 000279389200027 DOI 10.1021/cm100877h Anotace Nanocrystalline fibrous TiO2 (anatase) was prepared by electrostatic spinning from ethanolic solution of Ti(IV) butoxide, acetylacetone, and poly(vinylpyrrolidone) employing the Nanospider industrial process. These titania fibers were smoothly converted into cubic titanium oxynitride, TiOxNy fibers (a = 4.1930 angstrom) during 4 h at 600 degrees C in ammonia atmosphere. The obtained material is convertible back into TiO2 fibers by heat treatment in air at 500 degrees C. The TiO2 fibers, which were reformed in this way, contain anatase as the main phase. Their follow-up reaction with NH3 at 600 degrees C/2 h leads to a less crystalline oxynitride material with a approximate to 4.173 A, which is close to that of cubic TiO. Three subsequent cycles of this transformation were demonstrated. The described conversions are specific for electrospun anatase fibers only. At the same experimental conditions, other forms of nanocrystalline anatase do not react with ammonia yielding cubic phases. Pracoviště Ústav fyzikální chemie J.Heyrovského Kontakt Michaela Knapová, michaela.knapova@jh-inst.cas.cz, Tel.: 266 053 196 Rok sběru 2011
Počet záznamů: 1