Effect of ion irradiation on structure and thermal evolution of the Ni-C-60 hybrid systems

SYSNO ASEP	0346857
Druh ASEP	J - Článek v odborném periodiku
Zařazení RIV	J - Článek v odborném periodiku
Poddruh J	Článek ve WOS
Název	Effect of ion irradiation on structure and thermal evolution of the Ni-C-60 hybrid systems
Tvůrce(i)	Vacík, Jiří (UJF-V)_{RID, ORCID, SAI} Lavrentiev, Vasyl (UJF-V)_{RID, ORCID, SAI} Vorlíček, Vladimír (FZU-D)_RID Bačáková, Lucie (FGU-C)_{RID, ORCID} Narumi, K. (JP)
Zdroj.dok.	Nuclear Instruments & Methods in Physics Research Section B. - : Elsevier - ISSN 0168-583X Roč. 268, 11-12 (2010), s. 1976-1979
Poč.str.	4 s.
Akce	19th International conference on Ion beam analysis
Datum konání	07.09.2009-11.09.2009
Místo konání	Cambridge
Země	GB - Velká Británie
Typ akce	WRD
Jazyk dok.	eng - angličtina
Země vyd.	NL - Nizozemsko
Klíč. slova	Ion irradiation ; Fullerenes ; Nickel
Vědní obor RIV	JI - Kompozitní materiály
CEP	IAA200480702 GA AV ČR - Akademie věd
	IAA400100701 GA AV ČR - Akademie věd
	KAN400480701 GA AV ČR - Akademie věd
	LC06041 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy
CEZ	AV0Z10480505 - UJF-V (2005-2011)
	AV0Z10100520 - FZU-D (2005-2011)
	AV0Z50110509 - FGU-C (2005-2011)
UT WOS	000278702300062
DOI	10.1016/j.nimb.2010.02.112
Anotace	We report on the thermal response of the transition metal/fullerene thin hybrid multilayers, pristine and ion-modified, i.e., Ni/C-60/Ni and Ni/a-C/Ni (a-C amorphous carbon), both prepared on the MgO(1 0 0) monocrystalline substrate. The multilayer sequences were gradually annealed up to high temperatures and their structures were inspected using several analytical techniques. The inspection evidenced differences in the evolution of the virgin and ion-irradiated systems. In pristine (non-irradiated) composites (analyzed in the previous experiment) a significant part of the fullerene molecules out-diffused during annealing < 500 degrees C. At temperatures around (and above) 500 degrees C fullerenes underwent (in the vicinity of Ni) massive fragmentation and conversion to a-C. Very high temperature (1000 degrees C) annealing resulted in the fabrication of an array of micrometer-sized octagonal pits and rod-type particles emerging from the encompassing a-C + Ni mixture.
Pracoviště	Ústav jaderné fyziky