Influence of niobium alloying on the low cycle fatigue of cast TiAl alloys at room and high temperatures
- 1.
SYSNO ASEP 0346327 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Influence of niobium alloying on the low cycle fatigue of cast TiAl alloys at room and high temperatures Tvůrce(i) Kruml, Tomáš (UFM-A) RID, ORCID
Petrenec, Martin (UFM-A)
Obrtlík, Karel (UFM-A) RID, ORCID
Polák, Jaroslav (UFM-A) RID, ORCID
Buček, Petr (UFM-A)Celkový počet autorů 5 Zdroj.dok. Procedia Engineering. - Amsterdam : Elsevier BV
Roč. 2, č. 1 (2010), s. 2297-2305Poč.str. 9 s. Akce Fatigue 2010 Datum konání 06.06.2010-11.06.2010 Místo konání Praha Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova Low cycle fatigue ; lamellar TiAl alloy ; fracture surface Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP GA106/08/1631 GA ČR - Grantová agentura ČR GA106/07/0762 GA ČR - Grantová agentura ČR CEZ AV0Z20410507 - UFM-A (2005-2011) UT WOS 000278762900244 Anotace The low-cycle fatigue properties of TiAl alloys with 2 at.% and 7 at.% of Nb with nearly lamellar microstructure were studied at room temperature and 750 degrees C. Cyclic hardening/softening curves, cyclic stress-strain curves (CSSC) and fatigue life curves were obtained at both temperatures as well as monotonic tensile properties. Both materials show stable cyclic response at 750 degrees C. At room temperature, significant cyclic hardening characteristic for 2 at.% Nb alloy is not observed for 7 at.% Nb alloy. This difference is attributed to higher Nb content which increases the stacking fault energy and thus prevents intensive twinning. Parameters of the CSSC, the Manson-Coffin law and the Basquin law were determined. The cyclic strength of the alloy with 7 at.% Nb is substantially higher in comparison with 2 at.% Nb, probably due to lower thickness of the lamellas. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2011
Počet záznamů: 1