White-emitting oxidized silicon nanocrystals: Discontinuity in spectral development with reducing size
- 1.
SYSNO ASEP 0343173 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název White-emitting oxidized silicon nanocrystals: Discontinuity in spectral development with reducing size Tvůrce(i) Dohnalová, Kateřina (FZU-D) RID, ORCID
Ondič, Lukáš (FZU-D) RID, ORCID
Kůsová, Kateřina (FZU-D) RID, ORCID
Pelant, Ivan (FZU-D) RID, ORCID, SAI
Rehspringer, J.L. (FR)
Mafouana, R.-R. (FR)Zdroj.dok. Journal of Applied Physics. - : AIP Publishing - ISSN 0021-8979
Roč. 107, č. 5 (2010), 053102/1-053102/6Poč.str. 6 s. Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova silicon nanocrystals ; luminescence ; spectral shift Vědní obor RIV BM - Fyzika pevných látek a magnetismus CEP IAA101120804 GA AV ČR - Akademie věd LC510 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy KJB100100903 GA AV ČR - Akademie věd GA202/07/0818 GA ČR - Grantová agentura ČR CEZ AV0Z10100521 - FZU-D (2005-2011) UT WOS 000275657500003 DOI https://doi.org/10.1063/1.3289719 Anotace Small oxidized silicon nanocrystals of average sizes below 3.5 nm are prepared using modified electrochemical etching of a silicon wafer. Modifications introduced in the etching procedure together with postetching treatment in H2O2 lead to a decrease in the nanocrystalline core size and also, to some extent, to changes in the surface oxide. The interplay between these two factors allows us to blueshift the photoluminescence (PL) spectrum from 680 down to 590 nm, which is accompanied by changes in PL dynamics. This continual development, however, stops at about 590 nm, below which abrupt switching to fast decaying blue emission band at about 430 nm was observed. Discontinuity of the spectral shift and possible relation between both bands are discussed. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2011
Počet záznamů: 1