Deposition of gold nano-particles and nano-layers on polyethylene modified by plasma discharge and chemical treatment
- 1.
SYSNO ASEP 0332396 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Deposition of gold nano-particles and nano-layers on polyethylene modified by plasma discharge and chemical treatment Překlad názvu Deposice zlatých nano-částic a nano-vrstev na polyethylenu modifikovaném plasmatickým výbojem a chemickým působením Tvůrce(i) Švorčík, V. (CZ)
Chaloupka, A. (CZ)
Záruba, K. (CZ)
Král, V. (CZ)
Bláhová, O. (CZ)
Macková, Anna (UJF-V) RID, ORCID, SAI
Hnatowicz, Vladimír (UJF-V) RIDZdroj.dok. Nuclear Instruments & Methods in Physics Research Section B. - : Elsevier - ISSN 0168-583X
Roč. 267, č. 15 (2009), s. 2484-2488Poč.str. 5 s. Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova Polyethylene ; Plasma discharge ; Dithiol grafting Vědní obor RIV BG - Jaderná, atomová a mol. fyzika, urychlovače CEP LC06041 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy GA106/09/0125 GA ČR - Grantová agentura ČR CEZ AV0Z10480505 - UJF-V (2005-2011) UT WOS 000268617300005 DOI 10.1016/j.nimb.2009.05.071 Anotace Polyethylene (PE) was treated in Ar plasma discharge and then grafted from methanol solution of 1,2-ethanedithiol to enhance adhesion of gold nano-particles or sputtered gold layers. The modified PE samples were either immersed into freshly prepared colloid solution of Au nano-particles or covered by sputtered, 50 nm thick gold nano-layer. Properties of the plasma modified, dithiol grafted and gold coated PE were studied using XPS, UV-VIS, AFM, EPR, RBS methods and nanoindentation. It was shown that the plasma treatment results in degradation of polymer chain, creation of excessive free radicals and conjugated double bonds. After grafting with 1,2-ethanedithiol the concentration of free radicals declined but the concentration of double bonds remained unchanged. Plasma treatment changes PE surface morphology and increases surface roughness too. Another significant change in the surface morphology and roughness was observed after deposition of Au nano-particles. Pracoviště Ústav jaderné fyziky Kontakt Markéta Sommerová, sommerova@ujf.cas.cz, Tel.: 266 173 228 Rok sběru 2010
Počet záznamů: 1