Toughness versus stiffness of PP particulate composites modeling and experimental approach

    1.
    SYSNO ASEP0332105
    Druh ASEPA - Abstrakt
    Zařazení RIVNení vybrán druh dokumentu
    NázevToughness versus stiffness of PP particulate composites modeling and experimental approach
    Překlad názvuModelování a experimentální přístup určení vztahu mezi tuhostí versus pevností PP částicového kompozitu
    Tvůrce(i) Hutař, Pavel (UFM-A) RID, ORCID
    Majer, Zdeněk (UFM-A)
    Náhlík, Luboš (UFM-A) RID, ORCID
    Knésl, Zdeněk (UFM-A)
    Nezbedová, E. (CZ)
    Celkový počet autorů5
    Zdroj.dok.15th International Conference on Composite Structures. - Porto : University of Porto, 2009 / Ferreira Antonio
    S. 1-2
    Poč.str.2 s.
    Forma vydáníCD-ROM - CD-ROM
    AkceInternational Conference on Composite Structures /15./
    Datum konání15.6.2009-17.6.2009
    Místo konáníPorto
    ZeměPT - Portugalsko
    Typ akceWRD
    Jazyk dok.eng - angličtina
    Země vyd.PT - Portugalsko
    Klíč. slovaparticulate composite ; multiscale modeling ; fracture toughness ; stiffness
    Vědní obor RIVJL - Únava materiálu a lomová mechanika
    CEPKJB200410803 GA AV ČR - Akademie věd
    GA106/07/1284 GA ČR - Grantová agentura ČR
    CEZAV0Z20410507 - UFM-A (2005-2011)
    AnotaceThis contribution is focused on particulate composites, namely on composites with polypropylene matrix (PP) and rigid (CaCO3) fillers. Generally, the addition of rigid particles to a polymeric matrix has an embrittling effect on the composite. Using very fine isometric filler of sub-micron range with proper surface treatment and good final dispersion enable to achieve enhancement of toughness without significant reduction of its stiffness. The role of filler size and interphase properties on micro- and macro-behaviour of particulate composites is analysed from the experimental as well theoretical point of view. The attention is focused on fracture toughness and stiffness values. It is concluded that one of the possible sources of a toughening mechanism on micro- level is a blunting of the micro-crack caused by its interaction with coated particles. The results of numerical simulations are compared with relevant results determined experimentally.
    PracovištěÚstav fyziky materiálu
    KontaktYvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485
    Rok sběru2010
Počet záznamů: 1  

  Tyto stránky využívají soubory cookies, které usnadňují jejich prohlížení. Další informace o tom jak používáme cookies.

Přijmout všeNastaveníOdmítnout vše